Abstract:Hot-pressed and hot-deformed Nd-Fe-B magnets are generally made from rapidly quenched powder after crystallization treatment. In this work, the amorphous melt-spun ribbons are also employed directly as the precursor. The amorphous and crystallized powders with the composition of Nd28.47Pr0.56FebalB0.97Co3.63Al0.13Nb0.56Zr0.44 were employed for fabricating hot-pressed and hot-deformed magnets. The influences of processing parameters on the microstructure and magnetic properties have been investigated. For the hot-pressed magnets produced from both crystallized and amorphous powders, the grain pre-orientation and magnetic properties including coercivity, remanence and maximum energy product increase with the increasing temperature, pressure and holding time in the ranges of 650-800 oC, 300-600 MPa and 30-150 min, respectively. The hard magnetic properties of the hot-pressed magnets obtained from amorphous powder are slightly higher than those from crystalline powder due to the smaller grain size of the former. The magnetic properties of hot-deformed magnets are mainly determined by the deformation temperature and not influenced by the state of the powder and hot-pressed precursors. The hot-pressed magnets and hot deformed magnets with different microstructures exhibit different magnetization mechanisms. The optimal hot-deformation temperature is found to be 750 °C for obtaining a high maximum energy product of 39 MGOe. The present results suggest that the rapidly quenched amorphous powder can be used to not only directly prepare hot-pressed magnets with higher magnetic properties, but also to reduce the process step for hot-deformed Nd-Fe-B magnets.

Process of Hot Dip Zinc-Plating for Sintered NdFeB Magnets

Hot Dip Coating of 55Al-Zn for NdFeB Magnets

Influence of Hot-Pressing on Sintered Nd-Fe-B Permanent Magnets

Corrosion Protection of Nd-Fe-B Sintered Magnets by Aluminum Coating

Corrosion behavior of Nd-Fe-B sintered magnets at remanence state

Influence of Cladless Hot Isostatic Pressing on Magnetic Properties and Corrosion Resistance of Sintered NdFeB Magnets

Effect of electroless deposition on the corrosion resistance property for NdFeB permanent magnets with surface coating of Ni-P alloy

Microstructure and Property Evolution of Isotropic and Anisotropic Ndfeb Magnets Fabricated from Nanocrystalline Ribbons by Spark Plasma Sintering and Hot Deformation

Isotropic and Anisotropic Nanocrystalline NdFeB-Based Magnets Prepared by Spark Plasma Sintering and Hot Deformation

On the Cooling Rate of Strip Cast Ingots for Sintered NdFeB Magnets

Corrosion Behavior of Sintered NdFeB Magnets Coated with Ni Coatings Deposited by Ion Beam Sputtering

Improving the thermal stability of sintered NdFeB magnets with nickel electroplating by high temperature treatment

Diffusion of Nd-Rich Phase in the Spark Plasma Sintered and Hot Deformed Nanocrystalline Ndfeb Magnets

Magnetic microstructure and magnetic properties of spark plasma sintered NdFeB magnets

Properties Enhancement and Recoil Loop Characteristics for Hot Deformed Nanocrystalline Ndfeb Permanent Magnets

Properties of bulk magnets prepared by hot pressing using Zn- coated Sm-Fe-N magnetic powder by electrodeposition

Preparation of coatings with high adhesion strength and high corrosion resistance on sintered Nd–Fe–B magnets through electroless plating

Improved adhesion of electroless Ni-P coatings on sintered Nd-Fe-B magnets by pre-plating in ultrasonic field

Hot Deformed Anisotropic Nanocrystalline Ndfeb Based Magnets Prepared from Spark Plasma Sintered Melt Spun Powders

Comparison and process study of hot-pressed and hot-deformed Nd-Fe-B magnets prepared by amorphous and nanocrystalline powders

New Developments in NdFeB-Based Permanent Magnets