Comparison and process study of hot-pressed and hot-deformed Nd-Fe-B magnets prepared by amorphous and nanocrystalline powders

Ke Xu,Xuefeng Liao,Hongya Yu,Xichun Zhong,Zhongwu Liu,Guoqing Zhang

DOI: https://doi.org/10.1016/j.jmmm.2021.168193

IF: 3.097

2021-11-01

Journal of Magnetism and Magnetic Materials

Abstract:<p>Hot-pressed and hot-deformed Nd-Fe-B magnets are generally made from rapidly quenched powder after crystallization treatment. In this work, the amorphous melt-spun ribbons are also employed directly as the precursor. The amorphous and crystallized powders with the composition of Nd_28.47Pr_0.56Fe_balB_0.97Co_3.63Al_0.13Nb_0.56Zr_0.44 were employed for fabricating hot-pressed and hot-deformed magnets. The influences of processing parameters on the microstructure and magnetic properties have been investigated. For the hot-pressed magnets produced from both crystallized and amorphous powders, the grain pre-orientation and magnetic properties including coercivity, remanence and maximum energy product increase with the increasing temperature, pressure and holding time in the ranges of 650-800 ^oC, 300-600 MPa and 30-150 min, respectively. The hard magnetic properties of the hot-pressed magnets obtained from amorphous powder are slightly higher than those from crystalline powder due to the smaller grain size of the former. The magnetic properties of hot-deformed magnets are mainly determined by the deformation temperature and not influenced by the state of the powder and hot-pressed precursors. The hot-pressed magnets and hot deformed magnets with different microstructures exhibit different magnetization mechanisms. The optimal hot-deformation temperature is found to be 750 °C for obtaining a high maximum energy product of 39 MGOe. The present results suggest that the rapidly quenched amorphous powder can be used to not only directly prepare hot-pressed magnets with higher magnetic properties, but also to reduce the process step for hot-deformed Nd-Fe-B magnets.</p>

materials science, multidisciplinary,physics, condensed matter

What problem does this paper attempt to address?

The paper primarily explores the methods of preparing hot-pressed (HP) and hot-deformed (HD) Nd-Fe-B magnets using amorphous and nanocrystalline powders, and investigates the effects of different processing parameters on the microstructure and magnetic properties of the magnets.

Specifically, the researchers used two types of powders as raw materials: one was powder directly made from amorphous melt-spun ribbons; the other was powder after crystallization treatment. The composition of these two powders was Nd28.47Pr0.56FebalB0.97Co3.63Al0.13Nb0.56Zr0.44. By varying the temperature, pressure, and holding time during the hot-pressing process, as well as the deformation temperature during the hot-deformation process, the researchers analyzed how these factors influenced the final microstructure and magnetic properties of the magnets.

For hot-pressed magnets, regardless of whether crystalline or amorphous powders were used, the degree of particle pre-alignment and magnetic properties (including coercivity, remanence, and maximum energy product) improved with increasing temperature, pressure, and holding time. The hot-pressed magnets prepared using amorphous powders exhibited slightly higher hard magnetic properties, attributed to their smaller particle size.

For hot-deformed magnets, their magnetic properties were mainly determined by the deformation temperature, rather than the state of the powder or the state of the hot-pressed precursor. The optimal hot-deformation temperature was determined to be 750°C, at which a maximum energy product of up to 39 MGOe could be achieved.

In summary, the study demonstrated that rapidly quenched amorphous powders can not only be directly used to prepare hot-pressed magnets with higher magnetic properties but also simplify the steps in the preparation process of hot-deformed Nd-Fe-B magnets.