Microstructure refinement and significant improvements of magnetic properties in Pr2Fe14B/α-Fe nanocomposites
Z.Q. Jin,H. Okumura,Y. Zhang,H.L. Wang,J.S. Muñoz,G.C. Hadjipanayis
DOI: https://doi.org/10.1016/s0304-8853(02)00282-2
IF: 3.097
2002-07-01
Journal of Magnetism and Magnetic Materials
Abstract:Exchange coupled (Pr,Tb)2(Fe,Nb,Zr)14B/α-Fe nanocomposites have been produced by melt spinning. A trend for perpendicular and planar c-axis orientation of the 2:14:1 phase was observed in the free surface of ribbons spun at speeds below 10m/s and at optimal speeds, respectively. Higher wheel speeds led to the formation of an amorphous phase that transformed to 2:14:1 phase around 680°C. Optimum magnetic properties were found in samples spun at 14–17m/s and annealed at 700°C for 20min. The loop squareness was also found to depend mainly on the microstructure that is very sensitive to the sample composition. A few percentage of Nb and Zr suppressed the grain growth, resulting in a drastic improvement of magnetic properties, with approximate 50% enhancement in the intrinsic coercivity and an increase in maximum energy product from 5.6kOe and 14.7MGOe for the (Nb,Zr)-free sample to 8.2kOe and 20.3MGOe for the (Nb,Zr)-substituted samples, respectively. The significant improvement in magnetic properties originated from a much finer and homogeneous nanocomposite microstructure with an average grain size of 20nm, leading to a high remanence of 0.73 Ms. Henkel plots indicate the enhancement of exchange coupling between hard and soft magnetic phases.
materials science, multidisciplinary,physics, condensed matter