Microstructure and Phase Evolution Mechanism in Hot-pressed and Hot-deformed Nd-Fe-B Magnets with Nd85Cu15 Addition

Tieqiao Zhang,Wandong Xing,Fugang Chen,Shengsheng Liu,Lanting Zhang,Rong Yu
DOI: https://doi.org/10.1016/j.actamat.2020.116493
IF: 9.4
2021-02-01
Acta Materialia
Abstract:<p><a href="https://link_springer.xilesou.top/article/10.1007/s00410-002-0394-1">Chemical composition and structure characteristics of the intergranular phases</a> in Nd-Fe-B magnets play a key role in regulating the magnetic properties. However, it has still been a challenge to understand the evolution mechanism of grain boundary phases in hot-pressed and hot-deformed Nd-Fe-B magnets due to the complex phase composition and structure. In this work, grain boundary modification using Nd<sub>85</sub>Cu<sub>15</sub> alloy has been applied to hot-pressed and hot-deformed Nd-Fe-B magnets. The structure evolution mechanism of the grain boundary phase during hot-pressing was studied by TEM analysis, which shows that an overall reaction, Nd + Nd<sub>26</sub>Ga<sub>7</sub>Co<sub>10</sub> + Nd<sub>2</sub>Fe<sub>14</sub>B → Nd<sub>3</sub>Co + Nd<sub>5</sub>Fe<sub>2</sub>B<sub>6</sub> + Nd<sub>6</sub>(Fe,Co)<sub>13</sub>Ga, occurs at 600°C in hot-pressed magnet with Nd<sub>85</sub>Cu<sub>15</sub> addition. When the hot-deformation was conducted at 675°C abnormal grain growth was observed in hot-deformed magnets with or without Nd<sub>85</sub>Cu<sub>15</sub> addition. In contrast, as the hot deformation temperature decreased to 630 °C, the uniform and ultra-fine Nd<sub>2</sub>Fe<sub>14</sub>B grains formed in the Nd<sub>85</sub>Cu<sub>15</sub> doped magnet, which shows a significantly improved coercivity of 2.03 T and a squareness factor of 0.93.</p>
materials science, multidisciplinary,metallurgy & metallurgical engineering
What problem does this paper attempt to address?