Dependence of grain size and aspect ratio on grain boundary additives in hot-deformed Nd-Fe-B magnets

Xianshuang Xia,Mei Liu,Tieqiao Zhang,Qiang Dong,Lanting Zhang,Ligang Zhou,Mingqiang Li
DOI: https://doi.org/10.1016/j.matchar.2020.110543
IF: 4.537
2020-10-01
Materials Characterization
Abstract:<p>Commercial Nd<sub>13.6</sub>Fe<sub>73.6</sub>Ga<sub>0.6</sub>Co<sub>6.6</sub>B<sub>5.6</sub> (at.%) powders were mixed with 0-10 wt.% Nd<sub>80</sub>Cu<sub>15</sub>Al<sub>5</sub> alloy powders to prepare hot-deformed Nd-Fe-B magnets. As the increasing Nd<sub>80</sub>Cu<sub>15</sub>Al<sub>5</sub> content from 0 to 10 wt.%, the grain sizes along the c-plane (D<sub>||</sub>) decreased by more than 35% from 312 to 198 nm while the grain sizes along the ab-plane (D<sub>⊥</sub>) decreased by less than 7% from 58 to 54 nm, resulting in a decrease of more than 30% in the grain aspect ratio (D<sub>||</sub>/D<sub>⊥</sub>) from 5.4 to 3.7. Moreover, the temperature coefficient of coercivity increased significantly from -0.469 to -0.419%/°C by 8 wt.% Nd<sub>80</sub>Cu<sub>15</sub>Al<sub>5</sub> addition. Based on microstructure observations, the improved thermal stability of the magnets without using heavy rare-earth elements is due to combined effect of the exchange decoupling between grains by the nonferromagnetic grain boundary phases, the refinement of grains and the decreased grain aspect ratio.</p>
materials science, multidisciplinary,metallurgy & metallurgical engineering, characterization & testing
What problem does this paper attempt to address?