Ultrahigh coercivity and excellent thermal stability of hot-deformed Nd-Fe-B magnets by the diffusion of (Pr,Nd)-Dy-Cu-Al

Guantong wei,Min Zhao,Xianshuang Xia,Jinyun Ju,Yeyuan Du,Yiping Huang,Xu Tang,Wenzong Yin,Renjie Chen,Aru Yan

DOI: https://doi.org/10.1016/j.jallcom.2023.170756

IF: 6.2

2023-06-02

Journal of Alloys and Compounds

Abstract:The effects of the addition of (Pr 0.25 Nd 0.75 ) 10 Dy 80 Cu 5 Al 5 alloy powders on the magnetic properties and microstructure of the hot-deformed Nd-Fe-B magnets were investigated in this work. Through the addition of (Pr 0.25 Nd 0.75 ) 10 Dy 80 Cu 5 Al 5 , an ultrahigh coercivity of 3.14 T was obtained in a 6-mm-thick hot-deformed magnet, and the temperature coefficient of coercivity and remanence were improved from −0.475%/°C and −0.145%/°C to −0.383%/°C and −0.110%/°C at 20 −180 °C, respectively, showing the excellent thermal stability. Microstructure observations indicated that the formation of thick nonferromagnetic intergranular phase, the reduction of grain size and aspect ratio and the formation of the (Nd,Pr,Dy) 2 Fe 14 B main phase were achieved after the addition of (Pr 0.25 Nd 0.75 ) 10 Dy 80 Cu 5 Al 5 , which were the main reasons for the enhancement of coercivity and thermal stability.

materials science, multidisciplinary,chemistry, physical,metallurgy & metallurgical engineering