Abstract:Nanocrystalline Ce–Fe–B alloys exhibit potential utilization for low-cost permanent magnets, however, the preparation of anisotropic magnets with satisfactory magnetic properties remains a challenge. CeFe 2 Laves phase with high melting point that forms in the Ce-rich Ce–Fe–B magnets has been considered as the reason to be detrimental to its hot-working process and magnetic performance. Herein, we report the significant effects of adding Ga to nanocrystalline melt-spun Ce 17 Fe 78-x B 6 Ga x alloys on suppressing the CeFe 2 phase and enhancing coercivity. The x = 2.0 alloy is identified as the optimal precursor for preparing anisotropic hot-deformed magnet due to its lower CeFe 2 phase content (5.7 wt.%), considerably less than that of the ternary Ce–Fe–B alloy (17.6 wt.%). The congruent alignment and platelet-shaped grain characteristics are obtained in the Ga-added hot-deformed magnet, indicating an enhanced anisotropy that results in an improved remanence from 4.2 kGs to 5.9 kGs. The development of such texture can be ascribed to the reduced amount of CeFe 2 phase, allowing the formation of Ce-rich grain boundary (GB) phase, which is necessary to induce grain alignment during hot deformation process. Two types of Ga-containing GB phases are found in the Ga-added magnet, namely typical Ce-rich/Fe-lean GB phase and Ce 6 Fe 13 Ga phase. The uniformly distributed Ce-rich GB phases surrounding the main grains helps to magnetic isolate the Ce 2 Fe 14 B grains and thus enhance the coercivity, as verified by detailed microstructural characterizations combined with micromagnetic simulation. The work offers a potential way to realize anisotropy in Ce–Fe–B magnets and inspires further exploration of high abundance Ce-based magnets.

Structural evolution and improvement of magnetic properties of hot-deformed CeFeB magnets with Nd70Cu30 addition

Influence of Cu and Gd on Thermal Stability and Magnetic Properties of Nd(DyAl)FeB Magnets

Investigation of the magnetic properties, microstructure and corrosion resistance of sintered Nd-Ce-Fe-B magnets with different Ce contents

Effect of Nd-Co on microstructure and magnetic properties of Nd-Ce-Y-Fe-B sintered magnets

Optimization of the core-shell structures and grain boundary to improve the coercivity of high Ce-content Nd-Ce-Fe-B magnets

Magnetic Properties and Microstructure of Nanocrystalline Bulk Nd-Fe-B with Ce-Co Addition

Enhanced magnetic properties and anisotropy in hot-deformed Ce–Fe–B magnets by suppressing CeFe 2 phase with Ga addition

Study on Ce2Fe14B-based sintered magnets with Ce/RE> 80

Concurrent Improvements of Corrosion Resistance and Coercivity in Nd-Ce-Fe-B Sintered Magnets Through Engineering the Intergranular Phase

Strategy to improve magnetic property of sintered (Nd, Ce)–Fe–B magnets: Moderate replacement of cerium with lanthanum

Influence of Ce Content on the Rectangularity of Demagnetization Curves and Magnetic Properties of Re-Fe-B Magnets Sintered by Double Main Phase Alloy Method

Improvement of coercivity and its thermal stability of hot-deformed Nd-Fe-B magnets processed by Tb<sub>70</sub>Cu<sub>30</sub> doping and subsequent Nd<sub>85</sub>Cu<sub>15</sub> diffusion

Improvement of coercivity and its thermal stability of hot-deformed Nd-Fe-B magnets processed by Tb70Cu30 doping and subsequent Nd85Cu15 diffusion

Microstructure, coercivity and thermal stability of nanostructured (Nd,Ce)-(Fe,Co)-B hot-compacted permanent magnets

Effect of Heat Treatment on Microstructure and Magnetic Properties of Ce-Doped NdFeB Ribbons

Microstructure Evolution and Coercivity Enhancement in Hot-Deformed Nd-Fe-B Magnet Processed by Pr60Tb10Cu30 Diffusion

Enhanced Coercivity of Nd-Ce-Fe-B Sintered Magnets by Adding (nd, Pr)-H Powders

Ultrahigh coercivity and excellent thermal stability of hot-deformed Nd-Fe-B magnets by the diffusion of (Pr,Nd)-Dy-Cu-Al

The Effects of Forming CeFe2 on Phase Structure and Magnetic Properties in Ce-Rich Nd-Ce-Fe-B Permanent Magnetic Materials

High Cerium content Fe‐Ce‐Nd‐B sintered magnets with high coercivity

Microstructure and Phase Evolution Mechanism in Hot-pressed and Hot-deformed Nd-Fe-B Magnets with Nd<sub>85</sub>Cu<sub>15</sub> Addition