Effect of Ce content on the magnetic properties and microstructure of sintered Nd-Ce-Fe-B magnets after Pr 70 Cu 30 alloy diffusion
Fugang Chen,Hechang Han,Tieqiao Zhang,Yong Zhao,Xiaoli Wang,Wenqiang Zhao
DOI: https://doi.org/10.1016/j.jallcom.2022.165661
IF: 6.2
2022-05-31
Journal of Alloys and Compounds
Abstract:Grain boundary diffusion process (GBDP) with Pr 70 Cu 30 alloy was performed on sintered Nd-Ce-Fe-B magnets with different Ce contents (0 wt.%, 5 wt.%, 10 wt.% and 15 wt.%). The coercivities of the original magnets were 1053 kA/m (Ce: 0 wt.%), 912 kA/m (Ce: 5 wt.%), 915 kA/m (Ce: 10 wt.%) and 732 kA/m (Ce: 15 wt.%). After GBDP the coercivities were 1390 kA/m (Ce: 0 wt.%), 1074 kA/m (Ce: 5 wt.%), 937 kA/m (Ce: 10 wt.%) and 849 kA/m (Ce: 15 wt.%). Compared with the original magnets the coercivity increments were 337 kA/m (32%), 162 kA/m (17.8%), 22 kA/m (2.4%) and 117 kA/m (16%) for the magnets with Ce contents of 0 wt.%, 5 wt.%, 10 wt.% and 15 wt.%, respectively after GBDP. The Ce substitution for Nd/Pr promotes the diffusion process while the coercivity increment decreases due to the formation of abnormal coarse grains near the magnet surface. After GBDP the remanence increments were -0.01 T, 0.02 T, 0.04 T, 0.05 T for the Ce0, Ce5, Ce10 and Ce15 magnets, respectively. The improved remanence of the Nd-Ce-Fe-B magnets was attributed to the formation of Pr-rich grains near the magnet surface and the Pr-rich shells in the grain boundaries of the inner grains. The finding in this work reveals that for sintered Nd-Ce-Fe-B magnets the effect of GBDP is sensitive to the Ce content.
materials science, multidisciplinary,chemistry, physical,metallurgy & metallurgical engineering