Magnetic performance change of multi-main-phase Nd–Ce–Fe–B magnets by diffusing (Nd, Pr)H x

Tianyu Ma,Wenying Zhang,Baixing Peng,Yongsheng Liu,Yongjie Chen,Xinhua Wang,Mi Yan

DOI: https://doi.org/10.1088/1361-6463/aaa205

2018-01-01

Abstract:The grain boundary diffusion process (GBDP) is effective to enhance coercivity of the single-main-phase (SMP) RE2Fe14B (rare earth (RE)) magnets through forming magnetic hardening shells surrounding the hard grain cores. Here, the GBDP was applied to the multi-main-phase (MMP) (Nd, Pr)(22.3)Ce8.24Feba1M1.0B1.0 (wt.%) magnets prepared by sintering the mixture of Ce-free and Ce-containing 2:14:1 powders, which have shown superior magnetic properties, especially coercivity, to the SMP ones at the same average composition. The remanence of the (Nd, Pr)H-x diffused magnets increases gradually with the increase of diffusion temperature from 480 to 880 degrees C, the coercivity, however, slightly decreases. The highest (BH)(max) of 350.1 kJ m(-3) is achieved when diffusing at 680 degrees C, which is 9.2% higher than 320.7 kJ m(-3) for the as-prepared magnet. The remanence increment is due to the diffusion of Nd/Pr into the 2:14:1 phase grains, enlarging the intrinsic saturation magnetic polarization. The slight coercivity reduction is due to the gradual homogenization of RE distribution within the 2:14:1 grains of the undiffused parts, i.e. approaching the 'close to equilibrium (or SMP)'state, which offsets the positive contributions from the enrichment of Nd/Pr in the Ce-rich 2:14:1 phase and the formation of continuous RE-rich intergranular phase. These findings suggest that the GBDP effect on coercivity of the MMP Nd-Ce-Fe-B magnets is distinctly different from the SMP ones, and that the chemical heterogeneity should be carefully controlled to improve the magnetic properties of such high cost-performance permanent magnets.