Influence of grain size on susceptibility of ductility-dip crack on Ni-based high-temperature alloy

Jingqing CHEN,Hao LU,Hui CHEN,Guoqing GOU

DOI: https://doi.org/10.7512/j.issn.1001-2303.2015.06.06

2015-01-01

Abstract:Ni-based high-temperature alloy FM-52M(a filler metal of Inconel690) is widely applied on welding structure of nuclear power key component.However,a solid-state intergranular crack,called ductility-dip crack(DDC) is found in narrow gap filler weld of FM-52 M during the welding process of thick-wall pipeline.As the key component serves in a severe condition of high pressure and temperature and corrosive atmosphere,the existence of DDC will greatly affect the safety and life expansion of nuclear power plant.Thus the impulse TIG welding is introduced in this work to resolve the DDC defect during thick-wall pipeline welding of safety ending.Besides,a strain-to-fracture(STF) test based on Gleeble-3500 thermo-mechanical simulator is performed to evaluate the DDC susceptibility of FM-52 M.The results show that resistance of DDC of this deposited metal is improved by the refined microstructure by impulse TIG welding.