Abstract:Dissimilar metal welds (DMWs) between high-Cr martensitic heat-resistant steels and nickel-based alloys with nickel-based filler metals are widely used in fossil-fired power plants. Reports of premature failures of DMW joints have attracted considerable attention as such occurrences in the field can lead to significant economic loss and safety issues. Moreover, a comprehensive understanding of the high-temperature performance of new types of DMWs is lacking. In this work, creep tests were conducted over a stress range of 140-260 MPa at of 600 and 620 'C. A shift in the fracture location with variations in stress was observed, with three typical failure modes. At high stress levels (240-260 MPa), the DMW fractured in the base metal (BM) of martensitic steel, accompanied by a large degree of plastic deformation. At intermediate stress levels (200-240 MPa), the DMW fractured in the fine-grained heat-affected zone (FGHAZ) and the inter-critical heat-affected zone (ICHAZ), with creep cavities around coarsened carbides, indicating a typical type IV crack. At low stress levels (140-200 MPa), the DMW fractured in a mixed mode involving three stages. First, a crack initiated at the interface between the nickel-based weld metal and the martensitic steel, which was attributed to the interaction between the oxidation behavior of the martensitic steels and the thermal stress arising from the mismatch in the coefficients of thermal expansion. Second, the crack deflected into the FGHAZ/ICHAZ and developed into a type IV crack mode. Finally, the crack propagated into the adjacent BM, featuring significant plastic deformation. In addition, in the stress-LMP (Larson-Miller parameter) plot, the creep life at a relatively low stress level was shorter than that predicted by linear extrapolation of the data obtained at a high stress level, indicating a premature failure tendency at low stress. This premature failure tendency can be attributed to microstructure degradation in HAZs and preferential oxidation at the interface at low stress levels.

Weld Cracking Susceptibility of High-Cr Ni-Base Fe Alloys and Its Improvement—Development of Novel Test Method for Ductility-Dip Cracking and New Alloy

Influence of grain size on susceptibility of ductility-dip crack on Ni-based high-temperature alloy

Study on ductility-dip cracking susceptibility in filler metal 52M during welding

Study on Ductility Dip Cracking Susceptibility in Filler Metal 82 During Welding

Research Status of Ductility-Dip Crack Occurring in Nuclear Nickel-Based Welding Materials

Crack Susceptibility and Microstructure Analysis of Ni-based Alloy

Assessment of Ductility Dip Cracking Susceptibility on Ni Based Alloy by Fem Simulation

Multi-scale Study of Ductility-Dip Cracking in Nickel-Based Alloy Dissimilar Metal Weld

Welding hot cracking characteristics and fracture mechanisms of nickel‐based alloy NS1402 under different constraint conditions

Ductility Dip Cracking Mechanism of Ni–Cr–Fe Alloy Based on Grain Boundary Energy

High temperature damage development in Ni-alloy/steel dissimilar metal welds

Reduction of Ductility-Dip Cracking Susceptibility by Ultrasonic-Assisted Gtaw

Prevention of cold cracking by the welding process for reducing diffusible hydrogen in high-tensile thick plate welding

Mixed Mode Fatigue Crack Growth Behavior of Ni-Cr-Mo-V High Strength Steel Weldments

In-Situ Observations on the Fracture Mechanism of Diffusion-Alloyed Ni-Containing Powder Metal Steels and a Proposed Method for Tensile Strength Improvement

Numerical Investigation of Ductile Crack Growth Behavior in a Dissimilar Metal Welded Joint

In-situ Observation of Solidification Cracking of Laser Dissimilar Welded Joints

Fractal Analysis of Mo and Nb Effects on Grain Boundary Character and Hot Cracking Behavior for Ni-Cr-Fe Alloys

Alloy design of welding filler metal for 9Cr/2.25Cr dissimilar welded joint and mechanical properties investigation

An Experimental Investigation of In-Plane Constraint Effect on Local Fracture Resistance of A Dissimilar Metal Welded Joint

Fracture Location Shift of Dissimilar Metal Welds under Coupled Thermal-Stress Effect