Abstract:A magnesium–aluminum-layered double hydroxide (Mg-Al LDH) with a nano-lamellar morphology was prepared by using a homogeneous precipitation and hydrothermal method, and a calcination product (Mg-Al LDO) of the Mg-Al LDH was also obtained in this work. The XRD, TEM, SEM, FTIR, N2 ad/desorption, and TG-DTG techniques were employed to characterize the microstructures, morphologies, and thermostability levels of these two materials in detail. The results showed that both the Mg-Al LDH and Mg-Al LDO had mesoporous structures and nanoplate morphologies, with diameters of 50~200 nm. The Mg-Al LDH was transformed into Mg-Al LDO at 773 K in an air atmosphere. The adsorption properties of the Mg-Al LDH were investigated systematically with a copper chloride solution as a simulated waste. The experimental results demonstrated that the pH value of the solution had an obvious influence on its Cu2+ adsorption capacity, and the optimal pH value was approximately 5.0. The adsorption kinetics results showed that the Mg-Al LDH had a rapid adsorption rate, and the equilibrium adsorption capacity was 62.11 mg/g. Additionally, the Cu2+ adsorption could be commendably described using a pseudo-second-order model, demonstrating that the adsorption behavior is regulated by chemical sorption. The adsorption thermodynamic results indicated that the adsorption process was spontaneous at temperatures above 318 K. Moreover, the ΔG0 values decreased as the temperature was raised, which indicated that a higher temperature can cause a greater impetus for Cu2+adsorption. In addition, the positive values of the ΔH0 indicated that the Cu2+ adsorption was endothermic, and the positive ΔS0 values revealed an increase in the confusion at the solid–liquid interface of the adsorbent.

STUDY ON THE SYNTHESIS OF NiMgAl HYDROTALCITE-LIKE COMPOUNDS

Synthesis and Characterization of the Mixed Mg/Al Hydrotalcite‐Like Compounds

Synthesization and Characterization of Mg, Al- Hydrotalcites

Influence of Different Al Resources and Preparation Methods on the Synthesis of Mg-Al Hydrotalcite-like Compounds

Preparation, Characterization, and Catalytical Application of MgCoAl-Hydrotalcite-Like Compounds

Study on Mechanism Function of Thermal Decomposition of MgAl-hydrotalcite

Study of the Effects on Synthesis Mg-Al-hydrotalcite-like Compounds

Synthesis of Ca-Mg-Al Hydrotalcite-like Compounds and Application in the PVC

Study on Thermal Decomposition Process of MgAl-hydrotalcite

Synthesis and Characterization of MgAl-hydrotalcite and Its Intercalation Assembled Compound

Studies on Preparation and Crystal Structure of Ultrafine Particles Zn-Mg-Al-Hydrotalcite-like Compound

Structural characterization and thermal behavior of Ni/Mg/Al layered double hydroxides

Preparation and characterization of nickel-iron hydrotalcites and their derived mixed oxides

Preparation and Thermal Decomposition Properties of NiMn Layered Double Hydroxides by an Oxidation Precipitation Method

The Co-Precipitation Preparation and Properties of Inorganic Hydrotalcite

Hydrothermal Synthesis and Phase-, Morphology-Evolution Mechanism of Lead Titanate Nanostructures Assisted with Tetramethylammonium Hydroxide

Influence of Annealing Treatment on Microstructure and Cycling Stability of La-Rich Ml(Nicomnal)(5) Alloy Electrode for Ni/Mh Batteries

Preparation and Tribological Properties of Mg-Al Hydrotalcite-Like Compounds

Investigation of the physico-chemical properties of Ni-Mg-Al-La catalysts from ultrasound-assisted synthesis

Synthesis and Thermal Stability of Oxalate-intercalated Hydrotalcites

Synthesis of High-Crystallinity Mg-Al Hydrotalcite with a Nanoflake Morphology and Its Adsorption Properties for Cu2+ from an Aqueous Solution