Abstract:Calcium aluminate phases have a particular effect on the early heat release during setting initiation and have a substantial influence on the further workability of ordinary Portland cement. The nature of the calcium aluminate hydration products and its kinetics strongly depends on sulfate content and humidity. The effect of mineralisers on melt formation and viscosity is well described for calcium silicate systems, but information is still lacking for calcium aluminates. Therefore, the synergistic effect on the crystal structure and hydration mechanism of the tricalcium aluminate phase of the addition of mineralizers, i.e. Li 2 O, CuO, SO 3 to the raw meal is here investigated. Co-doped calcium aluminate structures were formed during high-temperature treatment. Thermal analysis (TG–DTA and heating microscopy) was used to describe the ongoing high-temperature reaction. Resulting phase composition was dependent on the concentration of the mineralizer. While phase pure system was prepared with low mineralizer concentrations, with increasing mineralizer content the secondary phases were formed. Raman spectroscopy and XPS analysis were used to investigate the cation substitution and to help describe the cations bonding in co-doped calcium aluminate system. Prepared powders have been hydrated in a controlled manner at different temperatures (288, 298, 308 K). The resulting calorimetric data have been used to investigate the hydration kinetics and determine the rate constant of hydration reaction. First-order reaction (FOR) model was here applied for the activation energy and frequency factor calculations. The metastable and stable calcium aluminate hydrates were formed according to initial phase composition. In phase pure systems with low S content, the formation of stable and metastable hydrates was depended on the reaction temperature. Conversely, in systems with secondary phases and higher S content, the hydration mechanism resembled that which appears in calcium sulfoaluminates.

Stability of hydrotalcite (Mg-Al layered double hydroxide) in presence of different anions

Thermochemical data and phase equilibria of halide (Cl−, Br−, I−) containing AFm and hydrotalcite compounds

Synthesis and Characterization of the Mixed Mg/Al Hydrotalcite‐Like Compounds

Synthesis and Thermal Stability of Oxalate-intercalated Hydrotalcites

Structure and Base Properties of Calcined Hydrotalcites

Insight into Metastable Lifetime of Α‐calcium Sulfate Hemihydrate in CaCl2 Solution

Synthesis of High-Crystallinity Mg-Al Hydrotalcite with a Nanoflake Morphology and Its Adsorption Properties for Cu2+ from an Aqueous Solution

Influences of Citric Acid on the Metastability of Α-Calcium Sulfate Hemihydrate in CaCl2 Solution

Adsorption of Nitrate and Nitrite from Aqueous Solution Onto Calcined (mg–al) Hydrotalcite of Different Mg/Al Ratio

Crystal chemistry of natural layered double hydroxides. 5. Single-crystal structure refinement of hydrotalcite, [Mg6Al2(OH)16](CO3)(H2O)4

Chemical and Structural Transformations of M-Al-CO3 Layered Double Hydroxides (M = Mg, Zn, or Co, M/Al = 2) at Elevated Temperatures: Quantitative Descriptions and Effect of Divalent Cations

Structural and Surface Acid/Base Properties of Hydrotalcite-Derived MgAlO Oxides Calcined at Varying Temperatures

Theoretical Studies On Layer Composition, Structure And Properties Of Hydrotalcite

Comprehensive Analysis of the Chemical and Structural Transformations of Mg–Al–CO3 Layered Double Hydroxides with Different Mg/Al Ratios at Elevated Temperatures

Study on Adsorption Properties of Calcined Mg–Al Hydrotalcite for Sulfate Ion and Chloride Ion in Cement Paste

Structure and CO2 Physisorption Capacity of Hydrotalcite-Derived Oxide

Investigation of the AFm-Cl system: Fe-to-Al solid solution, thermal behavior and carbonation

Synthesis and Surface Acid/Base Properties of Magnesium-Aluminum Mixed Oxides Obtained from Hydrotalcites

Hydration kinetics of C3A: effect of lithium, copper and sulfur-based mineralizers

Theoretical study on the structural properties and relative stability of M(II)-Al layered double hydroxides based on a cluster model.

Dehydration and Dehydroxylation of Layered Double Hydroxides: New Insights from Solid-State NMR and FT-IR Studies of Deuterated Samples