Abstract:We present the design and synthesis of Ca-rich Ca-Al-O oxides, with Ca(2+)/Al(3+) ratios of 1:1, 3:1, 5:1, and 7:1, which were prepared by hydrothermal decomposition of coprecipitated hydrotalcite-like Ca-Al-CO(3) precursors, for high-temperature CO(2) adsorption at 500-700 degrees C. In situ X-ray diffraction measurements indicate that the coprecipitated, Ca-rich, hydrotalcite-like powders with Ca(2+)/Al(3+) ratios of 5:1 and 7:1 contained Ca(OH)(2) and layered double hydroxide (LDH) phases. Upon annealing, LDH was first destroyed at approximately 200 degrees C to form an amorphous matrix, and then at 450-550 degrees C, the Ca(OH)(2) phase was converted into a CaO matrix with incorporated Al(3+) to form a homogeneous solid solution without a disrupted lattice structure. CaO nanocrystals were grown by thermal treatment of the weakly crystalline Ca-Al-O oxide matrix. Thermogravimetric analysis indicates that a CO(2) adsorption capacity of approximately 51 wt.% can be obtained from Ca-rich Ca-Al-O oxides prepared by calcination of 7:1 Ca-Al-CO(3) LDH phases at 600-700 degrees C. Furthermore, a relatively high CO(2) capture capability can be achieved, even with gas flows containing very low CO(2) concentrations (CO(2)/N(2)=10%). Approximately 95.6% of the initial CO(2) adsorption capacity of the adsorbent is retained after 30 cycles of carbonationcalcination. TEM analysis indicates that carbonation-promoted CaCO(3) formation in the Ca-Al-O oxide matrix at 600 degrees C, but a subsequent desorption in N(2) at 700 degrees C, caused the formation CaO nanocrystals of approximately 10 nm. The CaO nanocrystals are widely distributed in the weakly crystalline Ca-Al-O oxide matrix and are present during the carbonationcalcination cycles. This demonstrates that Ca-Al-O sorbents that developed through the synthesis and calcination of Ca-rich Ca-Al LDH phases are suitable for long-term cyclic operation in severe temperature environments.

Structure and Base Properties of Calcined Hydrotalcites

Structural and Surface Acid/Base Properties of Hydrotalcite-Derived MgAlO Oxides Calcined at Varying Temperatures

Synthesis and Surface Acid/Base Properties of Magnesium-Aluminum Mixed Oxides Obtained from Hydrotalcites

Effect of Mg/Al molar ratio on the basicity of Mg-Al mixed oxide derived from Mg-Al hydrotalcite

Exploration on influence of calcination temperature on structure and surface acidity and basicity of Mg(Al)O composite oxide

Formation of Base Sites on Calcined Mg−Ga Hydrotalcite-like [Mg1-xGax(OH)2](CO3)x/2·mH2O

Synthesis and Characterization of the Mixed Mg/Al Hydrotalcite‐Like Compounds

Stability of hydrotalcite (Mg-Al layered double hydroxide) in presence of different anions

Adsorption of Nitrate and Nitrite from Aqueous Solution Onto Calcined (mg–al) Hydrotalcite of Different Mg/Al Ratio

Synthesis and Characterization of Mn Intercalated Mg-Al Hydrotalcite.

Crystal chemistry of natural layered double hydroxides. 5. Single-crystal structure refinement of hydrotalcite, [Mg6Al2(OH)16](CO3)(H2O)4

Effect of the Na; CO; concentration on the preparation of hydrotalcite

Characterization and Structure Evolution of Ca-Al-CO3 Hydrotalcite Film for High Temperature CO2 Adsorption.

Synthesis of High-Crystallinity Mg-Al Hydrotalcite with a Nanoflake Morphology and Its Adsorption Properties for Cu2+ from an Aqueous Solution

Pillared hydrotalcite produced by calcine-recovering method and its structure characterization.

Preparation of Magnesium Aluminum Hydrotalcite with Orderly Porous Structure by Colloidal Crystal Template

SYNTHESIS OF MAGNESIUM-ALUMINUM MIXED OXIDE FROM HYDROTALCITE AND ITS PERFORMANCES AS CATALYTIC SUPPORT

Study on Adsorption Properties of Calcined Mg–Al Hydrotalcite for Sulfate Ion and Chloride Ion in Cement Paste

Ca-rich Ca-Al-oxide, high-temperature-stable sorbents prepared from hydrotalcite precursors: synthesis, characterization, and CO2 capture capacity.

Synthesis, Characterization And Isopropanol Catalytic Reaction Of Mg/Al,Co/Al And Co/Mg/Al Mixed Oxides From Hydrotalcite And Hydrotalcite-Like Precursors

THE SYNTHESIS AND CHARACTERIZATION OF CARBONATE PILLARED Co-Al HYDROTALCITE-LIKE COMPOUND