Abstract:Li(Ni0.5Co0.2Mn0.3)O2 layered materials were synthesized by solid-state reaction using Li2CO3 and three transition-metal hydroxide precursors of composition (Ni0.5Co0.2Mn0.3)(OH)2 (NMC Hydroxide) with different physical properties. Characterized by means of X-ray diffraction (XRD), scanning electron microscopy (SEM) and electrochemical testing, etc., the final Li(Ni0.5Co0.2Mn0.3)O2 products showed different physical and electrochemical properties depending on their synthesis temperatures and the properties of transition-metal hydroxide precursors were got. Higher reaction temperature results in bigger primary particle size (PPS) and broader size distribution. Precursor with smaller PPS results in larger PPS when synthesized at the same condition. The electrochemical performance is related to the physical properties of Li(Ni0.5Co0.2Mn0.3)O2. Better crystallized and cation ordered layered material has higher initial capacity while smaller and uniform PPS results in higher capacity retention rate. The Li(Ni0.5Co0.2Mn0.3)O2 synthesized at 880°C for 10h in atmosphere using (Ni0.5Co0.2Mn0.3)(OH)2 with smallest PPS size as the starting precursor showed the best overall electrochemical properties with a high discharge capacity over 171mAh/g with a capacity retention >96% after 50 cycles at 1C rate in a half battery and tap density about 2.7g/cm3.

Preparation and Thermal Decomposition Properties of NiMn Layered Double Hydroxides by an Oxidation Precipitation Method

Characterization of LiNi2 / 3Mn1 / 3O2 Prepared from NiMn layered double hydroxide

Hydrothermal Synthesis of Layer LiMnO2

Structural characterization and thermal behavior of Ni/Mg/Al layered double hydroxides

Hydrothermal Intercalation Reaction of Nickel Hydroxide into Layered Manganese Oxides

Nano-size MZnAl (m=cu, Co, Ni) Metal Oxides Obtained by Combining Hydrothermal Synthesis with Urea Homogeneous Precipitation Procedures

Temperature-dependence of calcination processes of Ni-rich layered oxides

Synthesis, Crystal structure and thermal reactivity of [(N2H5)2Mn0.20Ni0.80(C2O4)2](H2O)2: A novel precursor to nickel-manganese oxide

Preparation of LiNi_(0.5)Mn_(0.5)O_2 with Ni-Mn Hydrotalcite As Precursor and Effect of Excess Lithium on Its Electrochemical Performance

Effect of Calcining Temperature on the Structure and Electrochemical Performance of Li[Mn_(1/3)Ni_(1/3)Co_(1/3)]O_2

Effect of Calcining Temperature on the Structure and Electrochemical Performance of Li[Mn1/3Ni1/3C01/3]O2

Thermodynamic Analysis on the Coprecipitation of Ni-Co-Mn Hydroxide

Preparation and characterization of nickel-iron hydrotalcites and their derived mixed oxides

Preparation of Α-Mn2o3 and MnO from Thermal Decomposition of MnCO3 and Control of Morphology

The Preparation Process and Electrochemical Characteristics of Layer Structure LiNi1/3Co1/3Mn1/3O2 Cathode Materials

Effect of precursor and synthesis temperature on the structural and electrochemical properties of Li(Ni 0.5 Co 0.2 Mn 0.3 )O 2

Thermodynamic Analysis of Synthesis of Ni_(1/3)Co_(1/3)Mn_(1/3)(OH)_2 via Coprecipitation

Hydrothermally-assisted Co-Precipitation and Electrochemical Performance of LiNi1/3Co1/3Mn1/3O2 Cathode Material

Preparation of Cathode Materials LiNi_(1/3)Co_(1/3) Mn_(1/3)O_2 of Lithium Ion Battery by Electrolyzing NiCoMn Alloy

Preparation Of Nanocompound Oxide Limn2o4 And Characterization Of Its Electrochemical Properties

Synthesis and Phase Transition of Li–Mn–O Spinels with High Li/Mn Ratio by Thermo-Decomposition of LiMnC2O4(Ac)