Abstract:Ni-ferrite (NiFe2O4) powder was synthesized by a self-propagating high-temperature synthesis (SHS) process using Fe, Fe2O3 and various Ni-containing species (Ni-CSs) as reactants. The reactants were thoroughly mixed and pressed into a cylindrical compact. The compact was ignited by electrical heating under oxygen partial pressures varying between 0.02 and 1.5MPa. The effects of the type of Ni-containing species, the reactant composition, the oxygen pressure on the combustion temperature, and the product conversion were investigated. X-ray diffraction (XRD) analysis showed that oxygen pressure promoted product conversion. Among several Ni-containing species tested, Ni2O3 was found to give the highest conversion. The product conversion increased with increasing iron content and then decreased with further increase in iron content. Scanning electron microscope (SEM) observations showed that the product synthesized is mostly in the form of agglomerated fine particles with submicron size (0.1–0.5μm). Hysteresis behavior analysis showed that the product as synthesized possessed better soft magnetic properties when compared with commercial Ni-ferrite prepared by the solid reaction method.

Preparation of MnZn Power Ferrite by Self-Propagating High-temperature Synthesis Technology

Study on preparing Ni-Zn ferrites by SHS method

Self-propagating high temperature synthesis of Ni-Zn ferrite powder

Self-propagating High Temperature Synthesis of Ni0.35Zn0.65Fe2O4 Ferrite Powders

Self-Propagating High Temperature Synthesis of Ferrites

Preparation and Characterization of MnFe2O4 by a Microwave-Assisted Oxidative Roasting Process

STUDY ON SYNTHESIS OF Ni0.35Zn0.65Fe2O4 FERRITE BY SHS METHOD

Preparation and Properties of Nanosize MnZn Ferrite from Δ-Feooh

Synthesis of NiCuZn Ferrite Powders by SHS Method

Research Development of Preparation Technology of MnZn Ferrite

Self-propagating High Temperature Synthesis and Magnetic Properties of Ni 0.35 Zn 0.65 Fe 2 O 4 Powders

Study on Preparation of Mn-Zn Ferrite Materials by High-energy Ball Milling Method

High Tc, wide temperature ultrahigh Bs MnZn ferrite material and preparation method

Preparation of low-temperature sintered Mn doped Mg-Cu-Zn ferrites by sol-gel self-combustion method

Study on Zinc Volatilization in the Process of SHS Ni-Zn Ferrite Powder

Research Advancements and Developing Trends of MnZn Power Ferrites

High Density MnZn Magnetic Head Ferrite Prepared by Liquid-Phase Sintering Process

Self-propagating High Temperature Synthesis of Ni<SUB>0.35</SUB>Zn<SUB>0.65</SUB>Fe<SUB>2</SUB>O<SUB>4</SUB> using Various Ni-containing Species

Preparation of Phase Homogeneous Mn–Zn Ferrite Powder by Spray Pyrolysis

A self-propagating high-temperature synthesis method for Ni-ferrite powder synthesis

Research Advancements of MnZn Power Ferrite Materials