Sb2O3-doped Ni0.325Cu0.275Zn0.4Fe1.98O4 ferrite with enhanced permeability and larger cut-off frequency for high frequency low temperature co-fired electronic components
Shengye Wang,Yuanxun Li,Fuyu Li,Mingshan Qu,Yulong Liao,Qiye Wen
DOI: https://doi.org/10.1016/j.jmmm.2023.170773
IF: 3.097
2023-06-01
Journal of Magnetism and Magnetic Materials
Abstract:In order to solve the upper limit of device application frequency, it is urgent to develop new ferrites with high permeability and large cut-off frequency. Here, novel Sb2O3-doped NiCuZn ferrite ceramics (NCZF-x wt% Sb2O3, 0 ≤ x ≤ 0.35) were successfully fabricated via solid-state reaction method. This study found that Sb2O3, as an effective dopant, not only improved densification, but also contributed greatly to electro-magnetic properties. Especially, the permeability μ́ acquired the maximum value ∼ 210, and the cut-off frequency fr was 36 MHz at x = 0.05 wt%, while the dielectric loss tanδε was achieved 10–3 magnitude in the 10 ∼ 50 MHz. More importantly, the cut-off frequency fr with 134 MHz@x = 0.3 wt% and 129 MHz@x = 0.35 wt% were exceeded 120 MHz, which was significantly enhanced 4.47 ∼ 7.44 times than NiZnCo/NiCuZn ferrite. Outstanding electro-magnetic performance were achieved for NCZF-0.05/0.3 wt% Sb2O3: tanδε = 0.004@10 MHz, 0.008@50 MHz, μ́=210, fr = 36 MHz; tanδε = 0.02@10 MHz, 0.008@50 MHz, μ́=63, fr = 134 MHz, respectively. These excellent parameters in 0.05/0.3 wt% Sb2O3-doped NiCuZn ferrites were expected to be used as candidate materials in high-frequency electronic components.
materials science, multidisciplinary,physics, condensed matter