Preparation and characterization of Mn-Zn ferrite nanoparticles for tumor hyperthermia

路新丽,张东生,顾宁,郑杰,朱伟长,金立强,万美玲

DOI: https://doi.org/10.3321/j.issn:1001-0505.2004.01.019

2004-01-01

Abstract:With the sulfate as the materials and NaOH as precipitator, a series of MnxZn1-xFe2O4 nanoparticles (x=0.1, 0.3, ⋯, 0.9, 1.0) were produced, which are proved to be spinel Mn-Zn ferrite analyzed by X-ray diffraction (XRD). Their shapes are approximately global examined by transmission electron microscopy (TEM) and their average diameter is 30 nm measured with image analysis system. The Curie temperature was measured and in vitro heating test in a given alternating magnetic field was carried out. The results show that the Curie temperature increases with the reduction of the content of Zn and the steady temperature of the corresponding magnetic fluid in vitro heating test also increases along with the reduction of the content of Zn at 20 g/L. The steady temperature is between 40°C and 68°C. The results provide theoretical and practical evidence to select an appropriate value of x suitable for tumor hyperthermia.