Abstract:Beaded fiber composites represent ingenious design strategies capable of resolving the conflicts between strength and toughness in most engineering materials. Although intermittent beading holds great potential for improving mechanical properties, the underlying mechanisms responsible for strengthening and toughening of beaded fiber composites are largely unknown. In this study, we explore near-tip fields of an interface crack between the fiber and the polymeric bead, which is associated with fiber-bead debonding in the course of fiber pullout. The post-yield strain softening followed by strain hardening of polymer matrix, and friction between the bead and matrix are accounted for in the numerical analyses. It is found that pullout of fibers leads to development of multiple shear bands near the tip of the interface crack between the fiber and bead, and coalescence of shear bands gives rise to a zone of high plastic strain. Compared with the low level of friction between the bead and matrix, the bead-matrix interface with high friction coefficient can generate a larger zone of high plastic strain, increasing the propensity of interfacial debonding between the fiber and bead. Furthermore, we have revealed the role of thin coating of carbon nanotubes (CNT). Adding a CNT coating on the fiber enables the emergence of a small zone of high plastic strain near the interface crack tip and reduces the shear stress levels, thereby delaying bead debonding. Additionally, the introduction of CNT coating facilitates stress transfer from the bead to fiber, leading to high pullout force. The findings of this study provide important mechanistic insight into the design principles of beaded fiber composites.

Analysis for a Broken and Debonging Fiber in Ductile Matrix Composites

Micro Failure Analysis of Fiber Metal Laminates

Dynamic Tensile Behavior of Fiber Reinforced Materials Based on Fiber Layering Modeling

Cyclically Thermomechanical Plasticity Analysis for a Broken Fiber in Ductile Matrix Composites Using Shear Lag Model

Breakage of Beaded Fibers in a Polymer Matrix

Discrete Meso-Element Simulation of the Failure Behavior of Short-Fiber Composites under Dynamic Loading

Debonding mechanisms in the presence of an interphase in composites

Microscopic Progressive Damage Simulation of Unidirectional Composite Based on the Elastic–plastic Theory

Fiber Fragmentation by Twin-Fiber Bending Beam

Evaluation of Carbon Fiber/epoxy Interfacial Strength in Transverse Fiber Bundle Composite: Experiment and Multiscale Failure Modeling

Compressive Fatigue Damage and Failure Mechanism of Fiber Reinforced Cementitious Material with High Ductility

Experimental Study on the Mechanical Behavior and Failure Mechanism of 3d MWK Carbon/epoxy Composites under Quasi-Static Loading

Numerical Simulation of the Fiber Fragmentation Process in Single-Fiber Composites

Effect of interface damage on tensile behavior of fiber-reinforced ceramic-matrix composites after thermal fatigue loading

Micromechanical Modeling Tensile and Fatigue Behavior of Fiber-Reinforced Ceramic-Matrix Composites Considering Matrix Fragmentation and Closure

Analysis of fracture state and fatigue life of high modulus carbon fiber wrapped composite barrel

Interfacial crack-tip fields in beaded fiber composites

Meso-scale characterization and discrete element simulation of fiber-reinforced resin-mineral composite

A cohesive zone model for the elevated temperature interfacial debonding and frictional sliding behavior

Experimental investigation on the fatigue life and damage mechanism of plain weave composites under biaxial tension–torsion combined fatigue loading

Damage failure mechanism of unidirectional fiber reinforced SiC f /SiC composites under uniaxial tension