Abstract:Carbon-fiber reinforced composites are made up of three different phases. Tensile or compressive deformation in the longitudinal (fiber) orientation is controlled by the fibers, leading to a linear stress strain response which ends abruptly when the fibers fail by tensile fracture or kinking in compression. Conversely, major non-linear deformations can develop under transverse compression or in-plane shear because deformation is controlled by the polymeric matrix and the interphase.In this paper, first the V-notched rail shear test was used to research the mechanical properties of composite under in-plane shear loading, and the fracture surfaces of failed specimens were examined using scanning electron microscopy (SEM). The broken samples showed a large residual shear displacement. For [0/90](8s) cross-ply laminate V-notched beam test, the failure mode is the interactions of intralaminar and interlaminar failure. The intralaminar interfacial debonding, matrix cracking and interlaminar degradation occurs in succession. Then a representative volume element (RVE) of fiber random distribution was established, with two dominant damage mechanisms-matrix plastic deformation and interfacial debonding included in the simulation by the extended Drucker-Prager model and cohesive zone model respectively. The simulation results clearly reveal the damage process of the composites and the interactions of different damage mechanisms. It can be concluded that the in-plane shear fracture initiates as interfacial debonding and evolves as a result of interactions between interfacial debonding and matrix plastic deformation. The progressive damage process and final failure mode of in-plane shear model which are based on constitute are very consistent with the observed result under SEM of V-notched rail shear test. Also a transverse shear model was established as contrast in order to comprehensively understand the mechanical properties of composite materials under shear loading, and the progressive damage process and final failure mode of composite under transverse shear loading were researched.

Discrete Meso-Element Simulation of the Failure Behavior of Short-Fiber Composites under Dynamic Loading

Micro Failure Analysis of Fiber Metal Laminates

Progressive failure analysis of 2D woven composites at the meso-micro scale

Concurrent Multiscale Modeling of In-Plane Micro-Damage Evaluation in Z-pinned Composite Laminates

Failure Process Simulation of Concrete Structures Bydiscrete Element Method

Meso-scale characterization and discrete element simulation of fiber-reinforced resin-mineral composite

A 3D finite element model to simulate progressive damage in unidirectional- and woven-fibre thermoplastic discontinuous-long-fibre composites

Failure process simulation of concrete structures by discrete element method

Meso-scale modeling and damage analysis of carbon/epoxy woven fabric composite under in-plane tension and compression loadings

Microscopic Progressive Damage Simulation of Unidirectional Composite Based on the Elastic–plastic Theory

A new simulation method for characterizing the shear behavior of needled carbon fiber composites

Progressive Failure Analysis of Carbon Fiber/epoxy Composite Laminates Using Continuum Damage Mechanics

Visualization and interpretation of the impact failure behavior of textile composites using a highly efficient Meso-FE model

A Monte Carlo simulation of damage and failure process with crack saturation for unidirectional fiber reinforced ceramic composites

A double-phase field model for multiple failures in composites

Microscopic Progressive Damage And Failure Analysis Of Carbon-Fiber Reinforced Composite Under Shear Loading

Monte-Carlo Simulation on the Failure of Fiber in a Single Filament Composite

High-fidelity Simulations of Multiple Fracture Processes in a Laminated Composite in Tension

3D Mesoscale Fracture Analysis of Concrete under Complex Loading

A Discrete-Continuum Coupled Finite Element Model to Simulate All Failure Modes in Fibre Reinforced Concrete

A Monte Carlo finite element simulation of damage and failure in SiC/Ti–Al composites