Abstract:Yttrium oxide doped with europium has a great prospective for FED and PDP phosphor application. In present study, the precursor of yttrium oxide hydroxide nitrate nanorod, which was prepared via hydrothermal reaction route using PEG-6000 as template from the starting Y(NO3)(3) and KOH reactant system, was used to prepare Y2O3:Eu3+ nanorod via a post annealing process during which the precursor with adjustable shape and size was transformed to final Y2O3:Eu3+ product. XRD, field emission scanning electron microscopy (FE-SEM) and photoluminescence spectra (PL) were used to characterize the crystalline, morphology and luminescence properties of as-formed Y2O3:Eu3+ products synthesized at different post annealing temperatures, respectively. The results indicate that grain morphology of obtained Y2O3:Eu3+ product was nanorod with a mean diameter of about 40 similar to 60 nm and length of about 500 similar to 700 nm, the nanorod structure and morphology of obtained Y2O3:Eu3+ product maintained during post annealing process and the size varied slightly with different annealing temperatures. Pure cubic Y2O3:Eu3+ phase was formed and the size was the smallest at annealing treatment of 500 degrees C. Under the annealing temperature below 500 degrees C its diameter increased with increasing annealing temperature, and remained in a stable size when the annealing temperature was above 500 degrees C. The PL spectra of excitation spectra of Y2O3:Eu3+ product show that it exhibits excitation band located at about 395 and 468 nm, respectively. Above two excitation bands could be ascribed to the transition 4f-4f of Eu3+ ions in the Y2O3 host. On the other hand, the main emission peaks of the as-prepared products could be ascribed to the Eu3+ ions transition from D-5(0) to F-7(2). Furthermore, the luminescent intensity was improved about three times when the annealing temperature increased from 500 to 1000 degrees C.

Study on Technique of Preparation Non-Ball Grindery Red Phosphor Powder Y2O3:Eu3+ with Oxalic Acid Precipitation Method

Preparation of Y2o2s : Eu3+ Phosphors by A Novel Decomposition Method

Synthesis of Nanometer Y2o3 : Eu Phosphor and Its Luminescence Property

Preparation and Characterization of Y3Al5O12:Nd Phosphor Powders by Ultrasonic Atomization and Co-precipitation Process

Luminescent characterization of nano-Y2O3:Eu3+

Synthesis and photoluminescence of nano-Y2O3:Eu3+ phosphors

Two-steps Prepared Monodisperse Li-doped Y2O3:Eu3+ Microspheres and Their Luminescence Properties

Hydrothermal Method Synthesis and Characterization of Yvo4:Eu3+@Ypo4 Core-Shell Phosphor

Preparation And Luminescence Properties Of Y2o3 : Eu3+ Nanorods Via Post Annealing Process

SYNTHESIS OF Y_2O_3∶Eu NANOCRYSTALLINE BY COMPLEX PRECURSORS

Chemical Synthesis of a Blue‐Emitting NaSr1−X PO4:EuX Phosphor Powder

Luminescent Properties of Y2O3:Eu Synthesized by Sol–gel Processing

Rare-Earth-Doped Y4Al2O9 Nanoparticles for Stable Light-Converting Phosphors

Electro-deposition of Y2O3:Eu3+ thin film phosphor and its luminescent properties

Synthesis and Cathodoluminescent Properties of Y2O3: Eu3+ Phosphor with Micron-sized Controllable Particles

Synthesis, Structure and Spectrum Properties of Gd2O3:Er3+,Yb3+Nanometer Powder Coated with SiO2

General and Facile Method To Prepare Uniform Y<sub>2</sub>O<sub>3</sub>:Eu Hollow Microspheres

Yag : Ce3+ Nanopowders: Synthesis, Characteristics And Luminescent Properties

Chemical Synthesis of a Blue-Emitting NaSr<sub>1−X </sub>PO<sub>4</sub>:Eu<sub>X</sub>Phosphor Powder

Synthesis of Y3al5o12 : Eu3+ Phosphor by Sol-Gel Method and Its Luminescence Behavior

Eu2+ Activated Long Persistent Strontium Aluminate Nano Scaled Phosphor Prepared by Precipitation Method