Abstract:Yttrium oxide doped with europium has a great prospective for FED and PDP phosphor application. In present study, the precursor of yttrium oxide hydroxide nitrate nanorod, which was prepared via hydrothermal reaction route using PEG-6000 as template from the starting Y(NO3)(3) and KOH reactant system, was used to prepare Y2O3:Eu3+ nanorod via a post annealing process during which the precursor with adjustable shape and size was transformed to final Y2O3:Eu3+ product. XRD, field emission scanning electron microscopy (FE-SEM) and photoluminescence spectra (PL) were used to characterize the crystalline, morphology and luminescence properties of as-formed Y2O3:Eu3+ products synthesized at different post annealing temperatures, respectively. The results indicate that grain morphology of obtained Y2O3:Eu3+ product was nanorod with a mean diameter of about 40 similar to 60 nm and length of about 500 similar to 700 nm, the nanorod structure and morphology of obtained Y2O3:Eu3+ product maintained during post annealing process and the size varied slightly with different annealing temperatures. Pure cubic Y2O3:Eu3+ phase was formed and the size was the smallest at annealing treatment of 500 degrees C. Under the annealing temperature below 500 degrees C its diameter increased with increasing annealing temperature, and remained in a stable size when the annealing temperature was above 500 degrees C. The PL spectra of excitation spectra of Y2O3:Eu3+ product show that it exhibits excitation band located at about 395 and 468 nm, respectively. Above two excitation bands could be ascribed to the transition 4f-4f of Eu3+ ions in the Y2O3 host. On the other hand, the main emission peaks of the as-prepared products could be ascribed to the Eu3+ ions transition from D-5(0) to F-7(2). Furthermore, the luminescent intensity was improved about three times when the annealing temperature increased from 500 to 1000 degrees C.

Hydrothermal Method Synthesis and Characterization of Yvo4:Eu3+@Ypo4 Core-Shell Phosphor

Facile Synthesis and Luminescence Properties of Octahedral Yvo4:Eu3+ Microcrystals

Synthesis and Spectra Properties of YVO<SUB>4</SUB>:Eu Nanoparticles: Synthesis and Spectra Properties of YVO<SUB>4</SUB>:Eu Nanoparticles

Optical properties, energy transfer and thermal stability of spherical nano-phosphor YPO4:Eu3+:Sm3+

Hydrothermal synthesis and tunable luminescence of YPO4:Eu2+/Eu3+, Tb3+ nanocrystals

Fluorescent-magnetic Nanocrystals: Synthesis and Property of YP(x)V(1-x)O4:Eu@GdPO4 Core/shell Structure.

Influence of Concentration Effect and Au Coating on Photoluminescence Properties of YVO<sub>4</sub>:Eu<sup>3+</sup>Nanoparticle Colloids

Sol-gel Synthesis and Photoluminescence Properties of BaSO4/Y2O3:Eu3+ Core-Shell Submicrospheres

Synthesis and Photoluminescent Properties of NaYF<SUB>4</SUB>:Eu<SUP>3+</SUP> Core and NaYF<SUB>4</SUB>:Eu<SUP>3+</SUP>/NaYF<SUB>4</SUB> Core/Shell Nanocrystals

Hydrothermal Synthesis for the Enhanced Red and Green Sr3Y(PO4)(3):Eu3+, Tb3+ Phosphors

Hydrothermal Synthesis And Photoluminescence Of Eu2-Xsmxsn2o7 (X=0-2.0) Nanophosphors

Controllable Synthesis and Size-Dependent Luminescent Properties of YVO<sub>4</sub>:Eu<sup>3+</sup>Nanospheres and Microspheres

Fabrication, Patterning, and Optical Properties of Nanocrystalline YVO4:A (A = Eu3+, Dy3+, Sm3+, Er3+) Phosphor Films Via Sol−Gel Soft Lithography

Synthesis and Characterization of Monodispersed BaSO4/Y2O3:Eu3+ Core–shell Submicrospheres

Preparation And Luminescence Properties Of Y2o3 : Eu3+ Nanorods Via Post Annealing Process

Hydrothermal Synthesis and Characterization of Flowerlike YBO_3∶Eu~(3+)

Surfactant-free sacrificial template synthesis of submicrometer-sized YVO4:Eu3+ hierarchical hollow spheres with tunable textual parameters and luminescent properties.

SYNTHESIS OF Y_2O_3∶Eu NANOCRYSTALLINE BY COMPLEX PRECURSORS

Synthesis of Nanometer Y2o3 : Eu Phosphor and Its Luminescence Property

Two-steps Prepared Monodisperse Li-doped Y2O3:Eu3+ Microspheres and Their Luminescence Properties

Rare-Earth-Doped Y4Al2O9 Nanoparticles for Stable Light-Converting Phosphors