Abstract:Yttrium oxide doped with europium has a great prospective for FED and PDP phosphor application. In present study, the precursor of yttrium oxide hydroxide nitrate nanorod, which was prepared via hydrothermal reaction route using PEG-6000 as template from the starting Y(NO3)(3) and KOH reactant system, was used to prepare Y2O3:Eu3+ nanorod via a post annealing process during which the precursor with adjustable shape and size was transformed to final Y2O3:Eu3+ product. XRD, field emission scanning electron microscopy (FE-SEM) and photoluminescence spectra (PL) were used to characterize the crystalline, morphology and luminescence properties of as-formed Y2O3:Eu3+ products synthesized at different post annealing temperatures, respectively. The results indicate that grain morphology of obtained Y2O3:Eu3+ product was nanorod with a mean diameter of about 40 similar to 60 nm and length of about 500 similar to 700 nm, the nanorod structure and morphology of obtained Y2O3:Eu3+ product maintained during post annealing process and the size varied slightly with different annealing temperatures. Pure cubic Y2O3:Eu3+ phase was formed and the size was the smallest at annealing treatment of 500 degrees C. Under the annealing temperature below 500 degrees C its diameter increased with increasing annealing temperature, and remained in a stable size when the annealing temperature was above 500 degrees C. The PL spectra of excitation spectra of Y2O3:Eu3+ product show that it exhibits excitation band located at about 395 and 468 nm, respectively. Above two excitation bands could be ascribed to the transition 4f-4f of Eu3+ ions in the Y2O3 host. On the other hand, the main emission peaks of the as-prepared products could be ascribed to the Eu3+ ions transition from D-5(0) to F-7(2). Furthermore, the luminescent intensity was improved about three times when the annealing temperature increased from 500 to 1000 degrees C.

SYNTHESIS OF Y_2O_3∶Eu NANOCRYSTALLINE BY COMPLEX PRECURSORS

Nanosized Rare Earth Activated Phosphors

Synthesis of Nanometer Y2o3 : Eu Phosphor and Its Luminescence Property

Rare earth activated nanosized oxide phosphors: synthesis and optical properties

Preparation And Luminescence Properties Of Y2o3 : Eu3+ Nanorods Via Post Annealing Process

Local Structure and Luminescence of Nanocrystalline Y2O3:Eu

Synthesis and Properties of Europium-Based Phosphors on the Nanometer Scale: Eu2O3, Gd2O3:Eu, and Y2O3:Eu.

Low temperature chemical reaction synthesis of single-crystalline Eu(OH)<sub>3</sub> nanorods and their thermal conversion to Eu<sub>2</sub>O<sub>3</sub> nanorods

Synthesis Process and Luminescence Properties of Ln3+ Doped NaY(WO4)2 Nanoparticles

Synthesis of Y_2O_3:Yb,Er Nanocrystals by Complex Precipitation Method and Its Up-Conversion Luminescence Properties

Synthesis and photoluminescence of Eu3+-doped Y2Sn2O7 nanocrystals

Synthesis and luminescence properties of Y 2O 3:Eu with flower-like microstructure

Hydrothermal Method Synthesis and Characterization of Yvo4:Eu3+@Ypo4 Core-Shell Phosphor

Luminescent Properties of Li+ Doped Nanosized Y2O3:Eu

Spectrum characteristic and local structures of nanocrysalline Y2O3 :Eu3+

Upconversion Luminescence Properties of Y2o3:Yb, Er and Y2o2s:Yb, Er Nanoparticles Prepared by Complex Precipitation

Site-Selective Spectra and Time-Resolved Spectra of Nanocrystalline Y2o3 : Eu

Controlled Synthesis and Luminescent Properties of Cubic Lu2O3:Eu3+ Nanocrystals

Optical Properties of Nanocrystalline Y2O3:Eu3+

Hydrothermal synthesis and tunable luminescence of YPO4:Eu2+/Eu3+, Tb3+ nanocrystals

Size Dependence of Luminescent Properties for Hexagonal YBO3:Eu Nanocrystals in the Vacuum Ultraviolet Region