Abstract:Yttrium oxide doped with europium has a great prospective for FED and PDP phosphor application. In present study, the precursor of yttrium oxide hydroxide nitrate nanorod, which was prepared via hydrothermal reaction route using PEG-6000 as template from the starting Y(NO3)(3) and KOH reactant system, was used to prepare Y2O3:Eu3+ nanorod via a post annealing process during which the precursor with adjustable shape and size was transformed to final Y2O3:Eu3+ product. XRD, field emission scanning electron microscopy (FE-SEM) and photoluminescence spectra (PL) were used to characterize the crystalline, morphology and luminescence properties of as-formed Y2O3:Eu3+ products synthesized at different post annealing temperatures, respectively. The results indicate that grain morphology of obtained Y2O3:Eu3+ product was nanorod with a mean diameter of about 40 similar to 60 nm and length of about 500 similar to 700 nm, the nanorod structure and morphology of obtained Y2O3:Eu3+ product maintained during post annealing process and the size varied slightly with different annealing temperatures. Pure cubic Y2O3:Eu3+ phase was formed and the size was the smallest at annealing treatment of 500 degrees C. Under the annealing temperature below 500 degrees C its diameter increased with increasing annealing temperature, and remained in a stable size when the annealing temperature was above 500 degrees C. The PL spectra of excitation spectra of Y2O3:Eu3+ product show that it exhibits excitation band located at about 395 and 468 nm, respectively. Above two excitation bands could be ascribed to the transition 4f-4f of Eu3+ ions in the Y2O3 host. On the other hand, the main emission peaks of the as-prepared products could be ascribed to the Eu3+ ions transition from D-5(0) to F-7(2). Furthermore, the luminescent intensity was improved about three times when the annealing temperature increased from 500 to 1000 degrees C.

Luminescent Properties of Y2O3:Eu Synthesized by Sol–gel Processing

Synthesis of Nanometer Y2o3 : Eu Phosphor and Its Luminescence Property

Luminescent Properties of Y3al5o12:Eu3+ under Uv Region

Synthesis and Luminescence Properties of Red Long Afterglow Phosphor Y_2O_2S:Eu~(3+),Mg~(2+),Ti~(4+) by Sol-Gel Process

Morphology-tailored Synthesis and Luminescent Properties of Y 2 O 3 :Eu 3+ Phosphors

Synthesis and Iuminescent Properties of Y2O3 :Eu3+ Red Phosphor

Eu$lt;sup$gt;3+$lt;/sup$gt; Activated Y$lt;inf$gt;2$lt;/inf$gt;O$lt;inf$gt;3$lt;/inf$gt; Red Phosphor Monospheres: Size-controlled Processing and Luminescence Property

Synthesis of Y3al5o12 : Eu3+ Phosphor by Sol-Gel Method and Its Luminescence Behavior

Direct Synthesis and Intense Luminescence of Y2o3 : Eu Nanophosphors by Complexation Combustion

Synthesis and Luminescence Properties of Eu3+ -Doped Silicate Nanomaterial

Morphology-dependent crystallization and luminescence behavior of (Y,Eu)2O3 red phosphors

Patterning And Luminescent Properties Of Nanocrystalliney(2)O(3): Eu3+ Phosphor Films By Sol-Gel Soft Lithography

Synthesis and luminescent characteristic of Y2O2:Eu3+ nanocrystalline by mechanochemical process

Synthesis of Y2O3:Eu3+ phosphors by surface diffusion and their photoluminescence properties

Preparation And Luminescence Properties Of Y2o3 : Eu3+ Nanorods Via Post Annealing Process

Sol-Gel Synthesis And Luminescent Properties Of Red-Emitting Y(P,V)O-4:Eu3+ Phosphors

Sol–gel Combustion Synthesis and Luminescence of Y4Al2O9:Eu3+ Nanocrystal

Synthesis and Properties of Europium-Based Phosphors on the Nanometer Scale: Eu2O3, Gd2O3:Eu, and Y2O3:Eu.

Monodispersed colloidal spheres for uniform y2O 3:Eu3+ red-phosphor particles and greatly enhanced luminescence by simultaneous Gd3+ doping

Preparation and red long-afterglow luminescence of Y2O3: Eu, Dy

Preparation and luminescence of y2O3:Eu3+ nanopowder