Abstract:Novel SrEuBSiAlN phosphors were investigated as a function of the boron and aluminum over silicon ratio and as a function of the Eu concentration. Samples were prepared via solid-state reaction synthesis by carefully controlling the synthesis conditions and composition. At high boron and aluminum content, that is, x = 0, a Eu 5d-4f emission is observed of which the maximum shifts from 595 nm for low Eu concentrations (y = 0.005) toward 623 nm for high Eu concentrations (y = 0.5). The samples can be excited by UV or blue light up to ∼475 nm. Substitution of [BAl] units by [SiN] units, increasing x up to 0.15, greatly improves the luminescence efficiency up to 46% and shows a very large redshift of the excitation bands with ∼100 nm, while the emission band shifts with ∼10 nm. The shifts are attributed to the lowering of the 5d level as a result of the decreased Eu-N distance upon substitution. Temperature-dependent measurements show that the Eu 5d-4f emission is largely thermally quenched at room temperature for x = 0 due to thermal ionization toward the conduction band, explaining the low luminescence efficiency. The lowering of the 5d level at larger values of x reduces the thermal ionization and consequently increases the thermal stability and quantum efficiency, resulting in strongly luminescent blue-to-orange conversion phosphors that are interesting for light-emitting diode applications.

Blue-To-Orange Tunable Luminescence From Europium Doped Yttrium-Silicon-Oxide-Nitride Phosphors

Effects of Europium Content on Structures and Luminescence Properties of Tunable Light-Emitting Silicon Oxynitride Phosphors

Synthesis and spectral properties of rare-earth free tunable full-color-emitting Si-BCNO phosphors

Synthesis, Crystal Structure, and Luminescence Properties of Y4Si2O7N2: Eu2+ Oxynitride Phosphors

Color‐Tunable Emission Via Site‐Selective Occupation of Eu2+ Activators in Silicate Phosphors

Photoluminescence Tuning Via Energy Transfer in Eu-Doped Ba-2(Gd,Tb)(2)Si4o13 Solid-Solution Phosphors

Synthesis and Photoluminescence Properties of a Blue-Emitting La3Si8N11O4:Eu2+ Phosphor

Tunable Blue-Green-emitting Ca3Si2O4N2:Ce3+, Eu2+ Phosphor with Energy Transfer for Light-Emitting Diodes

Photoluminescence Tuning Via Energy Transfer in Eu-doped Ba2(Gd,Tb)2Si4O13 Solid-Solution Phosphors

Luminescence Properties and Energy Transfer Studies of A Color Tunable Bay2si3o10:Tm3+,Dy3+ Phosphor

Tunable Luminescence and Ce3+ → Tb3+ → Eu3+ Energy Transfer of Broadband-Excited and Narrow Line Red Emitting Y2SiO5:Ce3+, Tb3+, Eu3+ Phosphor

Synthesis and Luminescence Properties of A Blue-Emitting Sr3.5y6.5o2(Po4)1.5(Sio4)(4.5):Eu2+ Phosphor

Photoluminescence Properties of Y2SiO5 Doped with Eu3+ Phosphor

Intriguing Luminescence Properties of (ba, Sr) 3 Si 6 O 9 N 4 : Eu 2+ Phosphors Via Modifying Synthesis Method and Cation Substitution

Tunable Luminescence And Ce3+ -> Tb3+ -> Eu3+ Energy Transfer Of Broadband-Excited And Narrow Line Red Emitting Y2sio5:Ce3+, Tb3+, Eu3+ Phosphor

Eu 2+ -Doped Sr 2 B 2-2x Si 2+3x Al 2-x N 8+x : A Boron-Containing Orange-Emitting Nitridosilicate with Interesting Composition-Dependent Photoluminescence Properties.

Enhanced Emission from CaSi2O2N2:Eu2+ Phosphors by Doping with Y3+ Ions

Preparation And Luminescence Properties Of Red Phosphors Ca3y2si3o12:Eu3+

Synthesis, Persistent Luminescence, And Thermoluminescence Properties Of Yellow Sr3sio5:Eu2+, Re3+ (Re=Ce, Nd, Dy, Ho, Er, Tm, Yb) And Orange-Red Sr3-Xbaxsio5:Eu2+, Dy3+ Phosphor

Structure, Crystallographic Sites, And Tunable Luminescence Properties Of Eu2+ And Ce3+/Li+-Activated Ca1.65sr0.35sio4 Phosphors

Synthesis of a Broad-Band Excited and Multicolor Tunable Phosphor Gd2SiO5:Ce3+,Tb3+,Eu3+ for Near-Ultraviolet Light-Emitting Diodes