Influence of Anion/Cation Substitution (sr2+ → Ba2+, Al3+ → Si4+, N3– → O2–) on Phase Transformation and Luminescence Properties of Ba3Si6O15:Eu2+ Phosphors
Mengmeng Shang,Sisi Liang,Nianrui Qu,Hongzhou Lian,Jun Lin
DOI: https://doi.org/10.1021/acs.chemmater.6b05493
IF: 10.508
2017-01-01
Chemistry of Materials
Abstract:A series of promising cyan, green, and yellow emission (Ba, Sr)(3)(Si, Al)(6)(O, N)(15):Eu2+ phosphors were synthesized by a Pechini-type sol gel ammonolysis method. Variations in luminescence properties and crystal structure caused by the modification of phosphor composition were studied in detail. The prefired temperatures of the precursors play a key role in the process of forming the final products. Under UV light excitation, the as-prepared Ba3Si6O15:Eu2+ phosphor presents a strong ryan emission located at 498 nm. Moreover, the as-prepared oxynitride phosphors, Eu2+-activated (Ba1-ySry)(3)Si6-xAlxO15-mu,N-delta (x = 0-1.2, y = 0-0.6), display a broader excitation band covering the entire visible region. Under blue light excitation, Ba3Si6-xAlxO15-mu,N-delta:Eu2+ phosphors show a intense and narrow green emission at 520 nm, and the luminescent intensity can be enhanced by increasing Al content within a certain range. However, (Ba1-ySry)(3)Si6O15-mu,N-delta:Eu2+ phosphors exhibit green (520 nm) to yellow (554 nm) emission with increasing Sr content. Unexpectedly, Eu2+ doped Ba3Si6O9N4-type Ba3Si6O15-mu,N-delta-1300 degrees C phosphor exhibits a bluish green emission and strong thermal quenching behavior. The (Ba1-ySry)(3)Si6-xAlxO15-mu,N-delta:Eu2+ phosphors exhibit a small thermal quenching, and the quantum yields measured under 460 nm excitation could reach up to 89% for green Ba3Si6-xAlxO15-mu,N-delta:Eu2+ phosphor and 71% for yellow (Ba1-ySry)(3)Si6xO15-mu N delta:Eu2+ phosphor. White LEDs with tunable color temperature and higher color rendering index were fabricated by combining the prepared ryan Ba3Si6O15:Eu2+ green Ba2.91Eu0.09Si6-xAlxO15-mu,N-delta (x = 0.06)/yellow (Ba0.97-ySry)(3)Eu0.09Si6O15-mu,N-delta (y = 0.4) phosphor and a red phosphor with a UV or blue LED chip, indicating that they are promising phosphors for white LEDs.