Synthesis and luminous characteristics of a new (Y, Gd)(BO3, VO4):Eu phosphor
Chunting Shi,Chongfu Xu,Minli Yang
DOI: https://doi.org/10.3321/j.issn:1002-185x.2007.02.019
2007-01-01
Rare Metal Materials and Engineering
Abstract:The red fluorescence powder of Gd and Eu co-doped yttrium borovanadate was prepared for the first time by the modified solid state reaction method with the precursor synthesized by co-precipitates of ammonium oxalate and characterized with x-ray diffraction, emission and excitation spectra. Compared with (Y, Gd, Eu)VO4, the sample was impregnated with boric acid in the same number of moles as vanadium element, in which the boron element improves the emission intensity due to the BO33- imparting energy to Eu3+ without any lattice change of tetragonal (Y, Gd, Eu)VO4. Also, the optimum ratio of Gd3+ doped in the sample was ascertained according to the relative brightness for a series of samples. The effect of Gd3+ content on the emission intensity of the product was researched, and the mechanism that VO43- and BO33- transfer energy to Eu3+ was analyzed in this article. The luminescent characteristic of (Y, Gd, Eu)(BO3, VO4) was contrasted to (Y, Gd)VO4:Eu and (Y, Gd)BO3:Eu, separately. It can be concluded that the (Y, Gd, Eu)(BO3,VO4) possess better emission intensity and color purity as new type of fluorescent materials used for lamps and Plasma Display Panels. Also, comparing the modified method with the traditional solid state method, the reaction temperature descends for 100 degrees C, the luminous intensity increases in above 10 percent, the product is easier to comminute to be much smaller in diameter of the particles.