Abstract:Yttrium oxide doped with europium has a great prospective for FED and PDP phosphor application. In present study, the precursor of yttrium oxide hydroxide nitrate nanorod, which was prepared via hydrothermal reaction route using PEG-6000 as template from the starting Y(NO3)(3) and KOH reactant system, was used to prepare Y2O3:Eu3+ nanorod via a post annealing process during which the precursor with adjustable shape and size was transformed to final Y2O3:Eu3+ product. XRD, field emission scanning electron microscopy (FE-SEM) and photoluminescence spectra (PL) were used to characterize the crystalline, morphology and luminescence properties of as-formed Y2O3:Eu3+ products synthesized at different post annealing temperatures, respectively. The results indicate that grain morphology of obtained Y2O3:Eu3+ product was nanorod with a mean diameter of about 40 similar to 60 nm and length of about 500 similar to 700 nm, the nanorod structure and morphology of obtained Y2O3:Eu3+ product maintained during post annealing process and the size varied slightly with different annealing temperatures. Pure cubic Y2O3:Eu3+ phase was formed and the size was the smallest at annealing treatment of 500 degrees C. Under the annealing temperature below 500 degrees C its diameter increased with increasing annealing temperature, and remained in a stable size when the annealing temperature was above 500 degrees C. The PL spectra of excitation spectra of Y2O3:Eu3+ product show that it exhibits excitation band located at about 395 and 468 nm, respectively. Above two excitation bands could be ascribed to the transition 4f-4f of Eu3+ ions in the Y2O3 host. On the other hand, the main emission peaks of the as-prepared products could be ascribed to the Eu3+ ions transition from D-5(0) to F-7(2). Furthermore, the luminescent intensity was improved about three times when the annealing temperature increased from 500 to 1000 degrees C.

Microstructure and Photoluminescent Properties of Y2o3:Eu3+ Phosphors Synthesised by Precipitation and Combustion Methods

Hydrothermal Method Synthesis and Characterization of Yvo4:Eu3+@Ypo4 Core-Shell Phosphor

Hydrothermal Synthesis And Photoluminescence Of Eu2-Xsmxsn2o7 (X=0-2.0) Nanophosphors

Synthesis of Nanometer Y2o3 : Eu Phosphor and Its Luminescence Property

Two-steps Prepared Monodisperse Li-doped Y2O3:Eu3+ Microspheres and Their Luminescence Properties

Combustion synthesis and up-conversion luminescence of La 2 O 2 S:Er 3+ ,Yb 3+ nanophosphors

Combustion synthesis and up-conversion luminescence of La{sub 2}O{sub 2}S:Er{sup 3+},Yb{sup 3+} nanophosphors

Luminescent Properties of Li+ Doped Nanosized Y2O3:Eu

Preparation And Luminescence Properties Of Y2o3 : Eu3+ Nanorods Via Post Annealing Process

Solution Combustion Synthesis and Enhanced Luminescence of Eu3+-activated Y2Ce2O7 Phosphor Nanopowders

Rare earth activated nanosized oxide phosphors: synthesis and optical properties

Synthesis and luminescence properties of Y 2O 3:Eu with flower-like microstructure

Upconversion Luminescence Properties of Y2o3:Yb, Er and Y2o2s:Yb, Er Nanoparticles Prepared by Complex Precipitation

Synthesis and Upconversion Luminescence of Monodispersed, Submicron-Sized Er3+:Y2o3 Spherical Phosphors

Optimization of the Photoluminescence Properties of Electrodeposited Y[sub 2]o[sub 3]:Eu[sup 3+] Thin-Film Phosphors

Luminescent Properties of Y2O3:Eu Synthesized by Sol–gel Processing

Synthesis of Y3al5o12 : Eu3+ Phosphor by Sol-Gel Method and Its Luminescence Behavior

Local Structure and Luminescence of Nanocrystalline Y2O3:Eu

Electro-deposition of Y2O3:Eu3+ thin film phosphor and its luminescent properties

SYNTHESIS OF Y_2O_3∶Eu NANOCRYSTALLINE BY COMPLEX PRECURSORS

Synthesis and Properties of Europium-Based Phosphors on the Nanometer Scale: Eu2O3, Gd2O3:Eu, and Y2O3:Eu.