Photoluminescence of Y2O2S: Eu3+ Phosphor Prepared by Flux Fusion Method

WANG Zhi-long,WANG Yu-hua
DOI: https://doi.org/10.3321/j.issn:1001-9731.2005.09.006
2005-01-01
Abstract:Single phase of Y_2O_2S∶Eu~(3+)_x(0.01≤x≤0.10) was prepared by the flux fusion method and their photoluminescence were investigated.The result indicated that the unit cell parameter c was linear increased with the increasing of Eu_2O_3 content in Y_2O_2S∶Eu(0.01≤x≤0.10).On the other hand,the changing of unit cell parameter a isn't a linear dependence.Under 330nm excitation,the emission spectrum of Y_2O_2S∶Eu~(3+)_x(0.01≤x≤0.10) were similarly and the strongest intensity emission peak was observed at about 540nm or 626nm.With the increasing of Eu_2O_3 content,the position of strongest intensity emission peak moved form 540nm(~5D_1→~7F_2 transition) to 626nm(~5D_0→~7F_2 transition),and the maximum intensity emission was obtained when x=0.09 in Y_2O_2S∶Eu~(3+)_x(0.01≤x≤0.10).This result is explained in terms of the environment of trivalent europium in the crystal structure of Y_2O_2S.Long afterglow properties of Y_2O_2S∶Eu~(3+) doped with Mg~(2+),Ti~(4+) were under currently investigated.
What problem does this paper attempt to address?