Peculiar β-Li 2 TiO 3 : Eu 3+ red light emitting dominated by electric dipole transition: Asymmetric lattice point regulation and luminescence performance
Cheng-Long Yu,Guan-Hua Liu,Dang-Bo Jin,Hang Cheng,Yong Qi,Zi-Hang Liu,Zhi-Qi Wang,Hai Li,Dan-Peng Gao,Xiu-Feng Wang
DOI: https://doi.org/10.2139/ssrn.4536156
IF: 6.2
2023-11-28
Journal of Alloys and Compounds
Abstract:In order to obtain red phosphor with high color purity, β-Li 2 TiO 3 : Eu 3+ dominated by electric dipole transition was prepared by the hydrothermal method. Eu 3+ doping concentration ( 12 h) can regulate the phase purity, supercell development, asymmetric lattice point configuration and the luminescence performance. Under excitation at 394 nm, β-Li 2 TiO 3 : Eu 3+ emits narrow band 618 nm red light due to that Eu 3+ replaces Li + at the relatively active Li1 position, and the 5 D 0 → 7 F 2 electric dipole transition dominates. Calcined at 600 °C for 36 h with Eu 3+ doped concentration of 0.5 mol%, the luminescence performance of β-Li 2 TiO 3 : Eu 3+ is superior, of which the lifetime is 0.64 ms, the color coordinates x = 0.63, y = 0.37, the color temperature of 987 K, the color rendering index of 82, and the red color purity of 99.7%. The electric dipole transition line intensity parameters Ω 2 and Ω 4 are 8.01 × 10 −20 cm 2 and 0.62 × 10 −20 cm 2 , respectively, yielding Ω 2 /Ω 4 of 12.9. The fluorescence branch ratio of 5 D 0 → 7 F 2 is 82.9%, and the quantum efficiency can reach 92%, which is superior within similar materials.
materials science, multidisciplinary,chemistry, physical,metallurgy & metallurgical engineering