Abstract:Tb3+ and Yb3+ codoped Lu2O3 nanophosphors were synthesized by the reverse-strike co-precipitation method. The obtained Lu2O3:Tb3+,Yb3+ nanophosphors were characterized by X-ray diffraction (XRD) and photoluminescence (PL) spectra. The XRD results showed that all the prepared nanophosphors could be readily indexed to pure cubic phase of Lu2O3 and indicated good crystallinity. The Tb3+→Yb3+ energy transfer mechanisms in the UV-blue region in Lu2O3 nanophosphors were investigated. The experimental results showed that the strong visible emission around 543 nm from Tb3+ (5D4→7F5) and near-infrared (NIR) emission around 973 nm from Yb3+ (2F5/2→2F7/2) of Lu2O3:Tb3+,Yb3+ nanophosphors were observed under ultraviolet light excitation, respectively. Tb3+ could be effectively excited up to its 4f75d1 state and relaxed down to the 5D4 level, from which the energy was transferred cooperatively to two neighboring Yb3+. The Yb3+ concentration dependent luminescent properties and lifetimes of both the visible and NIR emissions were also studied. The lifetime of the visible emission decreased with the increase of Yb3+ concentration, verifying the efficient energy transfer from the Tb3+ to the Yb3+. Cooperative energy transfer (CET) from Tb3+ to Yb3+ was discussed as a possible mechanism for the near-infrared emission. When doped concentrations were 1 mol.% Tb3+ and 2 mol.% Yb3+, the intensity of NIR emission was the strongest.

Cooperative Energy Transfer in Eu3+, Yb3+ Codoped Y2O3 Phosphor

Cooperative Energy Transfer in Tb3+/Yb3+- and Nd3+/Yb3+/Tb3+-Codoped Oxyfluoride Glasses

Sensitized Yb3+ Luminescence of Eu3+/Yb3+‐Codoped Fluorosilicate Glass Ceramics

Energy Transfer and Frequency Upconversion in Er3+-Yb3+ Codoped Oxy-Fluoro-tungstosilicate Glasses

Quantum Cutting Downconversion by Cooperative Energy Transfer from Bi 3+ to Yb 3+ in Y 2 O 3 Phosphor

Cooperative Energy Transfer and Frequency Upconversion in Yb 3+ –tb 3+ and Nd 3+ –yb 3+ –tb 3+ Codoped GdAl 3 (BO 3 ) 4 Phosphors

Energy Transfer in Tb3+,Yb3+ Codoped Lu2O3 Near-Infrared Downconversion Nanophosphors

Up-conversion Luminescence Performance of Yb 3+ , Er 3+ /ho 3+ Co-Doped Y 2 W 3 O 12 Phosphors

Strong Dependence of Upconversion Luminescence on Doping Concentration in Holmium and Ytterbium Co-Doped Y 2 O 3 Phosphor

The Energy Transfer of Bi3+ → Eu3+ and Bi3+ → Tb3+ in YBO3 Host to Produce Light

Ultraviolet and visible upconversion emission in Tb 3+ /Yb 3+ co-doped fluorophosphate glasses

Synthesis and upconversion luminescent properties of Er 3+ doped and Er 3+-Yb 3+ codoped GdOCl powders

Ultraviolet and visible upconversion emission in Tb<sup>3+</sup>/Yb<sup>3+</sup> co-doped fluorophosphate glasses

Energy Transfer Mechanisms in Yb3+-Doped Gdvo4 Near-Infrared Downconversion Nanophosphor

Investigation of Energy Transfer in Pr3+, Yb3+ Co-Doped Phosphate Phosphor: the Role of 3P0 and 1D2

Cooperative Energy Transfer Frequency Upconversion in Tb3+/Yb3+-codoped Oxyfluoride Glasses

Effect of Eu 3 + Codoping on Upconversion Luminescence in Y 2 O 3 : Er 3 + , Yb 3 + Nanocrystals

Optical Transition and Upconversion Luminescence in Er3+ Doped and Er3+–Yb3+ Co-Doped Fluorophosphate Glasses

Energy Transfer Mechanisms in Yb3+ Doped YVO4 Near-Infrared Downconversion Phosphor

Energy Transfer in Ce, Nd, and Yb Co-Doped YAG Phosphors

Spectral Variations and Energy Transfer Processes on Both Er3+ Ion Concentration and Excitation Densities in Yb3+–Er3+ Codoped LaF3 Materials