Structure and Spectral Properties of NaY<sub>2</sub>F<sub>7</sub>:Eu<SUP>3+</SUP>/Eu<SUP>2+</SUP> Transparent Glass-Ceramics
Hu Fangfang,Gong Hailin,Wang Jie,Wei Rongfei,Guo Hai
DOI: https://doi.org/10.3788/LOP202158.1516020
2021-01-01
Laser & Optoelectronics Progress
Abstract:In this paper, NaY2F7 Eu transparent glass-ceramics were successfully synthesized through high temperature melting method. X-ray diffraction, transmission electron microscopy, and selected electron diffraction showed that the NaY2F7 nanocrystals were formed and uniformly dispersed in the glass matrix, with particle sizes ranging from 31 nm to 38 nm. Under the excitation of 340 nm, the blue band emission of Eu-2(+) was observed, and the peak value was 425 nm, indicating that Eu3+ was reduced to Eu-2(+) in the air atmosphere. Excited at 393 nm, the sample has a strong red emission, and Eu3+ emission peaks at 577, 589, 612, 650, and 701 nm were observed in the emission spectrum. By changing the excitation wavelength (340 - 400 nm), the emission color of NaY2F7:Eu transparent glass-ceramics can he adjusted from blue to red region. Under the excitation of 380 nm, the emission intensity of GC-660 sample at 413 K is 75.1% of that at 313 K. The results indicate that NaY2F7:Eu2+/Eu-3(+) glass ceramics have great potential applications in plant lighting.