Upconversion luminescence and temperature sensing properties of Yb2(MoO4)3:Ln3+ (Ln = Ho, Tm, Er) phosphors based on energy transfer
Huimin Du,Yunhao Liang,Xingzuo Liu,Yue Deng,Jie Yang,Jun Yang,Shanshan Hu,yue Deng
DOI: https://doi.org/10.1039/d3ce00497j
IF: 3.756
2023-09-15
CrystEngComm
Abstract:Yb 2 (MoO 4 ) 3 :Ln 3+ (Ln = Ho, Tm, Er) phosphors were synthesized by a hydrothermal method with further calcination. The crystal structure and morphology of the samples were characterized by X-ray diffraction and scanning electron microscopy. The effects of rare earth ion interaction in the Yb 2 (MoO 4 ) 3 :Ln 3+ phosphors on the upconversion (UC) luminescence properties and energy transfer process at different doping concentrations were discussed. It is concluded that by doping Ho 3+ , Tm 3+ , and Er 3+ in the Yb 2 (MoO 4 ) 3 host, the phosphors emit orange-yellow, blue and green light, respectively, and the energy transfer from Yb 3+ → Ho 3+ /Er 3+ and Yb 3+ → Tm 3+ is a two and three photon process, respectively. Under the excitation of a 980 nm laser, by changing the Ho 3+ /Tm 3+ ratio in doped Yb 2 (MoO 4 ) 3 , we have realized the transition of phosphors from cold white light to warm white light. The temperature sensitivity of the 2 H 11/2 and 4 S 3/2 energy levels of Yb 2 (MoO 4 ) 3 :Er 3+ in the range of 323–573 K was studied by the FIR technology. The experimental results show that the maximum absolute sensitivity was 0.0081 K −1 at 573 K and the maximum relative sensitivity was 0.01 K −1 at 323 K. Compared with other materials, the Er 3+ doped Yb 2 (MoO 4 ) 3 phosphor is an excellent optical temperature sensing material.
chemistry, multidisciplinary,crystallography