The synthesis and luminescence properties of efficient Ba5 Zn4 Y8 O21∶Er3+/Yb3+ upconversion phosphor

Nan ZHANG,Yao FU,Mingming XING,Xixian LUO

DOI: https://doi.org/10.3969/j.issn.1001-9731.2016.10.024

2016-01-01

Abstract:A novel Ba5 Zn4 Y8 O21∶Er3+,Yb3+ upconversion phosphor has been synthesized by solid phase meth-od.XRD and SEM measurement results show that the phosphor crystalized well and presented granular appear-ance with average particle size of 1-5μm.Under the excitation of 980 nm laser,extremely bright orange lumi-nescence can be observed.Spectral test results confirm that the emission peaks are located in 520-530 nm,530-550 nm and 650-690 nm.The green emissions originate from the populations of 2 H11/2 and 4 S3/2 energy levels, and the subsequent transitions to the ground state.The red emission is mainly related to the cross relaxation of 4 I11/2 (Er3+)+4 F7/2 (Er3+)→4 F9/2 (Er3+)+4 F9/2 (Er3+)and the reverse energy transfer of 4 S3/2 (Er3+)+ 2 F7/2 (Yb3+)→4 I13/2 (Er3+)+ 2 F5/2 (Yb3+),as well as the transitions of 4 I13/2→4 F9/2 and 4 F9/2→4 I15/2 .Due to the cross relaxation and reverse energy transfer,the red emission intensity can be effectively improved and the green emission can be reduced,so that the red emission intensity can reach 6-1 3 times of the green emission intensity. The best doping concentration of Er3+ was 3mol% under the condition of 7mol% Yb3+ doping content.Impro-ving the power density of excitation light can not only enhance the UCL,but also improve the intensity ratio of red and green light.Under high power excitation,the blue and blue-green emissions caused by three photon ab-sorption can also be observed.