Abstract:A novel Ba5 Zn4 Y8 O21∶Er3+,Yb3+ upconversion phosphor has been synthesized by solid phase meth-od.XRD and SEM measurement results show that the phosphor crystalized well and presented granular appear-ance with average particle size of 1-5μm.Under the excitation of 980 nm laser,extremely bright orange lumi-nescence can be observed.Spectral test results confirm that the emission peaks are located in 520-530 nm,530-550 nm and 650-690 nm.The green emissions originate from the populations of 2 H11/2 and 4 S3/2 energy levels, and the subsequent transitions to the ground state.The red emission is mainly related to the cross relaxation of 4 I11/2 (Er3+)+4 F7/2 (Er3+)→4 F9/2 (Er3+)+4 F9/2 (Er3+)and the reverse energy transfer of 4 S3/2 (Er3+)+ 2 F7/2 (Yb3+)→4 I13/2 (Er3+)+ 2 F5/2 (Yb3+),as well as the transitions of 4 I13/2→4 F9/2 and 4 F9/2→4 I15/2 .Due to the cross relaxation and reverse energy transfer,the red emission intensity can be effectively improved and the green emission can be reduced,so that the red emission intensity can reach 6-1 3 times of the green emission intensity. The best doping concentration of Er3+ was 3mol% under the condition of 7mol% Yb3+ doping content.Impro-ving the power density of excitation light can not only enhance the UCL,but also improve the intensity ratio of red and green light.Under high power excitation,the blue and blue-green emissions caused by three photon ab-sorption can also be observed.

Up-conversion luminescence of Y2O3: Yb, Er under 1.55 μm excitation

Upconversion Emission Colour Modulation of Y2O2S: Yb, Er under 1.55μm and 980nm Excitation

Highly Efficient Saturated Visible Up-Conversion Photoluminescent Y2o3:Er3+ Microspheres Pumped With A 1.55 Mu M Laser Diode

Highly efficient saturated visible up-conversion photoluminescent Y<sub>2</sub>O<sub>3</sub>:Er<sup>3+</sup> microspheres pumped with a 1.55 μm laser diode

Upconversion Photoluminescence Properties of SrY2O4:Er3+,Yb3+ under 1550 and 980 Nm Excitation

High-purity and Color-tunable Up-conversion Luminescence of YVO4∶ Yb3 +,er 3 + Nanoparticles

Up-Conversion Luminescence of Nay(Wo4)(2): Yb, Er under 1550 and 980 Nm Excitation

The synthesis and luminescence properties of efficient Ba5 Zn4 Y8 O21∶Er3+/Yb3+ upconversion phosphor

High-Purity Red Up-Conversion Emission of Ba5zn4y8o21:Er3+,Yb3+ Phosphor Excited by 1550 Nm Laser Diode

Upconversion Luminescence of Y2Ti2O7:Er3+ under 1550 and 980 Nm Excitation

Simultaneous improvement in emission intensity and spectral purity of red photon upconversion in Gd2O3:Yb3+/Er3+ phosphors under 1550 nm excitation

Upconversion of oxide Y2O3 doped with (Yb3+ , Er3+) ions with 978 nm excitation]

Single red up-conversion emission of Er3+, Tm3+ co-doped NaYF4 nano-particles under 1510 nm excitation

Enhancing Red Luminescence by Doping Yb3+ into Er3+ Self-Sensitized Gd2O2S Upconverting Nanoparticles under Excitation at 1530 Nm

Single Red Up-Conversion Luminescence of Er Sensitized Layered Y2Ti2O7 Phosphor

Simple method for simultaneously achieving red and green up-conversion luminescence

Enhanced Green Up-Conversion Luminescence in In2O3:Yb3+/Er3+ by Tri-Doping Zn2+

Up-conversion Properties in KGd2F7:Yb3+/Er3+

High Color Purity Red Emission of Y2ti2o7:Yb3+, Er3+ under 1550 and 980 Nm Excitation

Upconversion luminescence mechanisms of Er(3+) ions under excitation of an 800 nm laser.

Near-infrared to visible upconversion in Er 3+ and Yb 3+ codoped Lu 2O 3 nanocrystals: Enhanced red color upconversion and three-photon process in green color upconversion