Abstract:The Y2O2S:Er3+@Y2O2S:Yb3+,Tm3+ core-shell upconversion (UC) nanoparticles with average diameter of 95 nm were synthesized by the homogeneous co-precipitation method combining with the solid-gas sulfidation route. The increases of nanocrystaline size after the shell coating was observed both in the X-ray diffraction (XRD) and transmission electron microscope (TEM) measurements. This indicates the composition homogeneity core-shell Y2O2S nanocrystals. Meanwhile, the luminescence of both the Er3+ and Tm3+ ions are realized for the first time in the novel core-shell Y2O2S:Er3+@Y2O2S:Yb3+,Tm3+ nanoparticles under the excitations of both 980 and 1550 nm. When excited by a 980 nm laser diode, the Y2O2S:Er3+@Y2O2S:Yb3+,Tm3+ phosphor exhibits blue (approximate to 475 nm), green (approximate to 548 nm) and red (approximate to 670 nm) emissions in the visible region, which correspond to the (1)G(4) -> H-3(6) transition of Tm(3+)ions, S-4(3/2), H-2(11/2) -> I-4(15/2) and F-4(9/2) -> I-4(15/2) transitions of Er3+ ions, respectively. The very strong emission at the near infrared (NIR) region is mainly due to the H-3(4) -> H-3(6) transition of Tm3+ ions. The emission from both of Era} and Tm3+ ions under 980 nm excitation reveals the energy transfers of Yb3+ -> Tm3+ within the shell layer and Yb3+ -> Er3+ between the shell and the core. When pumping at 1550 nm, although only Er3+ ions can efficiently absorb the excitation energy, the strong UC emissions from Tm3+ ions were also observed. This is owing to the energy transfer between the core and the shell through Er3+ -> Yb3+ -> Tm3+ ions. (C) 2016 Elsevier B.V. All rights reserved.

Upconversion Emission Colour Modulation of Y2O2S: Yb, Er under 1.55μm and 980nm Excitation

Up-conversion luminescence of Y2O3: Yb, Er under 1.55 μm excitation

Upconversion Photoluminescence Properties of SrY2O4:Er3+,Yb3+ under 1550 and 980 Nm Excitation

Upconversion of oxide Y2O3 doped with (Yb3+ , Er3+) ions with 978 nm excitation]

Preparation of Gd2O2S:Er3+,Yb3+ phosphor and its multi-wavelength sensitive upconversion luminescence mechanism

Energy Transfer and Frequency Upconversion in Er3+-Yb3+ Codoped Oxy-Fluoro-tungstosilicate Glasses

High-purity and Color-tunable Up-conversion Luminescence of YVO4∶ Yb3 +,er 3 + Nanoparticles

The Preparation and the Up and Down-Conversion Luminescence of Y_2O_2S∶Er,Yb Nanocrystals

Upconversion Multicolor Tuning: Red To Green Emission From Y2o3:Er, Yb Nanoparticles By Calcination

Blue, green, red upconversion luminescence and optical characteristics of rare earth doped rare earth oxide and oxysulfide

Synthesis and characterization of Y 2O 3:Er 3+ upconversion materials with nanoporous structures

Upconversion Luminescence Properties of Y 2 O 2 S:Er 3+ @Y 2 O 2 S:Yb 3+ ,tm 3+ Core-Shell Nanoparticles Prepared Via Homogeneous Co-Precipitation

Up-Conversion Luminescence of Nay(Wo4)(2): Yb, Er under 1550 and 980 Nm Excitation

Upconversion Luminescence of Y2Ti2O7:Er3+ under 1550 and 980 Nm Excitation

Luminescence Spectroscopy and Near-Infrared to Visible Upconversion in Er3+ and Yb3+ Codoped Sc2O3 Nanoparticles

Tunable Upconversion Luminescence of Monodisperse Y2O3: Er3+/Yb3+/Tm3+ Nanoparticles

Enhancing Red Luminescence by Doping Yb3+ into Er3+ Self-Sensitized Gd2O2S Upconverting Nanoparticles under Excitation at 1530 Nm

The Upconversion Luminescence of Er3+/Yb3+ -Codoped Oxyfluorosilicate Glasses

Significant Enhancement of Visible Up-Conversion Emissions of Y2O2S:Er3+ Phosphors by Mn2+ Sensitizing under 1550 Nm Excitation

Size-Dependent Upconversion Luminescence in Er3+/Yb3+-Codoped Nanocrystalline Yttria: Saturation and Thermal Effects

Upconversion Emission in Tm/Er/Yb Co‐Doped Yttria Stabilized Zirconia Single Crystals