Abstract:Yttrium oxide doped with europium has a great prospective for FED and PDP phosphor application. In present study, the precursor of yttrium oxide hydroxide nitrate nanorod, which was prepared via hydrothermal reaction route using PEG-6000 as template from the starting Y(NO3)(3) and KOH reactant system, was used to prepare Y2O3:Eu3+ nanorod via a post annealing process during which the precursor with adjustable shape and size was transformed to final Y2O3:Eu3+ product. XRD, field emission scanning electron microscopy (FE-SEM) and photoluminescence spectra (PL) were used to characterize the crystalline, morphology and luminescence properties of as-formed Y2O3:Eu3+ products synthesized at different post annealing temperatures, respectively. The results indicate that grain morphology of obtained Y2O3:Eu3+ product was nanorod with a mean diameter of about 40 similar to 60 nm and length of about 500 similar to 700 nm, the nanorod structure and morphology of obtained Y2O3:Eu3+ product maintained during post annealing process and the size varied slightly with different annealing temperatures. Pure cubic Y2O3:Eu3+ phase was formed and the size was the smallest at annealing treatment of 500 degrees C. Under the annealing temperature below 500 degrees C its diameter increased with increasing annealing temperature, and remained in a stable size when the annealing temperature was above 500 degrees C. The PL spectra of excitation spectra of Y2O3:Eu3+ product show that it exhibits excitation band located at about 395 and 468 nm, respectively. Above two excitation bands could be ascribed to the transition 4f-4f of Eu3+ ions in the Y2O3 host. On the other hand, the main emission peaks of the as-prepared products could be ascribed to the Eu3+ ions transition from D-5(0) to F-7(2). Furthermore, the luminescent intensity was improved about three times when the annealing temperature increased from 500 to 1000 degrees C.

Synthesis of Y2O3:Eu3+ coated Y 2O3 phosphors by urea-assisted homogeneous precipitation and its photoluminescence properties

Synthesis of Nanometer Y2o3 : Eu Phosphor and Its Luminescence Property

Electro-deposition of Y2O3:Eu3+ thin film phosphor and its luminescent properties

Two-steps Prepared Monodisperse Li-doped Y2O3:Eu3+ Microspheres and Their Luminescence Properties

Hydrothermal Method Synthesis and Characterization of Yvo4:Eu3+@Ypo4 Core-Shell Phosphor

Synthesis and Properties of Europium-Based Phosphors on the Nanometer Scale: Eu2O3, Gd2O3:Eu, and Y2O3:Eu.

Luminescent Properties of Y2O3:Eu Synthesized by Sol–gel Processing

Preparation And Luminescence Properties Of Y2o3 : Eu3+ Nanorods Via Post Annealing Process

High Quality Thin Film Phosphors of Y2o3:Eu3+ Deposited Via Chemical Bath Deposition

Synthesis and luminescent properties of Ba3Y3.88Gd0.12O9:Eu3+ phosphors with enhanced red emission

Optimization of the Photoluminescence Properties of Electrodeposited Y[sub 2]o[sub 3]:Eu[sup 3+] Thin-Film Phosphors

A Garnet-Based Ca2YZr2Al3O12:Eu3+ Red-Emitting Phosphor for N-Uv Light Emitting Diodes and Field Emission Displays: Electronic Structure and Luminescence Properties

Preparation and Properties of Ti, Eu Co-Doped Y2O2S:0.06Ti,0.08Eu Phosphor with Red Long Afterglow

Synthesis and luminescence properties of Y 2O 3:Eu with flower-like microstructure

SYNTHESIS OF Y_2O_3∶Eu NANOCRYSTALLINE BY COMPLEX PRECURSORS

Formation mechanism and red light emission photoluminescence of single-phase crystalline Eu2O2CO3 nanoplates compared with Y2O3:Eu phosphor

Synthesis and Luminescence Properties of New Red-Emitting Phosphors YGe0.5M0.5O4:Eu3+ (m=mo, W)

Upconversion Luminescence Properties of Y2o3:Yb, Er and Y2o2s:Yb, Er Nanoparticles Prepared by Complex Precipitation

Combinatorial Study of the Optimization of Y2O3:Bi,Eu Red Phosphors

Facile synthesis and luminescence properties of uniform and well-dispersed YF 3:Eu 3+ architectures

Rare-Earth-Doped Y4Al2O9 Nanoparticles for Stable Light-Converting Phosphors