Abstract:Yttrium oxide doped with europium has a great prospective for FED and PDP phosphor application. In present study, the precursor of yttrium oxide hydroxide nitrate nanorod, which was prepared via hydrothermal reaction route using PEG-6000 as template from the starting Y(NO3)(3) and KOH reactant system, was used to prepare Y2O3:Eu3+ nanorod via a post annealing process during which the precursor with adjustable shape and size was transformed to final Y2O3:Eu3+ product. XRD, field emission scanning electron microscopy (FE-SEM) and photoluminescence spectra (PL) were used to characterize the crystalline, morphology and luminescence properties of as-formed Y2O3:Eu3+ products synthesized at different post annealing temperatures, respectively. The results indicate that grain morphology of obtained Y2O3:Eu3+ product was nanorod with a mean diameter of about 40 similar to 60 nm and length of about 500 similar to 700 nm, the nanorod structure and morphology of obtained Y2O3:Eu3+ product maintained during post annealing process and the size varied slightly with different annealing temperatures. Pure cubic Y2O3:Eu3+ phase was formed and the size was the smallest at annealing treatment of 500 degrees C. Under the annealing temperature below 500 degrees C its diameter increased with increasing annealing temperature, and remained in a stable size when the annealing temperature was above 500 degrees C. The PL spectra of excitation spectra of Y2O3:Eu3+ product show that it exhibits excitation band located at about 395 and 468 nm, respectively. Above two excitation bands could be ascribed to the transition 4f-4f of Eu3+ ions in the Y2O3 host. On the other hand, the main emission peaks of the as-prepared products could be ascribed to the Eu3+ ions transition from D-5(0) to F-7(2). Furthermore, the luminescent intensity was improved about three times when the annealing temperature increased from 500 to 1000 degrees C.

Preparation methods of novel structural Y2O3:Eu3+

Hydrothermal Method Synthesis and Characterization of Yvo4:Eu3+@Ypo4 Core-Shell Phosphor

Preparation of Y2o2s : Eu3+ Phosphors by A Novel Decomposition Method

Synthesis of Y2O3:Eu3+ phosphors by surface diffusion and their photoluminescence properties

Synthesis of Y2O3:Eu3+ coated Y 2O3 phosphors by urea-assisted homogeneous precipitation and its photoluminescence properties

Microstructure and Photoluminescent Properties of Y2o3:Eu3+ Phosphors Synthesised by Precipitation and Combustion Methods

Morphology-tailored Synthesis and Luminescent Properties of Y 2 O 3 :Eu 3+ Phosphors

Luminescent Properties of YVO 4 :Eu/sio 2 Core–shell Composite Particles

Synthesis and Properties of Core Shell Sio2@Y2o3:Eu3+ Wavelength Conversion Materials

Preparation And Luminescence Properties Of Y2o3 : Eu3+ Nanorods Via Post Annealing Process

Synthesis and photoluminescence of nano-Y2O3:Eu3+ phosphors

Preparation and luminescence of y2O3:Eu3+ nanopowder

Synthesis, Crystal Structure, and Luminescence Properties of Y4Si2O7N2: Eu2+ Oxynitride Phosphors

Synthesis and luminescence properties of Y 2O 3:Eu with flower-like microstructure

Two-steps Prepared Monodisperse Li-doped Y2O3:Eu3+ Microspheres and Their Luminescence Properties

Synthesis and Photoluminescence of SrY2O4:Eu3+ Superfine Phosphor

Preparation and Luminescence of Y<sub>2</sub>O<sub>3</sub>:Eu<sup>3+</sup> Nanopowder

Synthesis of Y2Si2O7:Eu Nanocrystal and Its Optical Properties

Preparation and red long-afterglow luminescence of Y2O3: Eu, Dy

Close-Relationship Between the Luminescence and Structural Characteristics in Efficient Nanophosphor Y2mo4o15:Eu3+

Synthesis and Luminescent Properties of Monodisperse Core–shell Structured SiO2@Lu2O3:Eu3+ Microspheres