Abstract:The effect of solo and combined addition of Al (3wt. %) and Zn (1wt. %) into gravity-cast Mg-10 wt. % Sn binary alloy on the dry sliding wear test has been investigated using pin-on-disk configuration with varying rotational speed (100 and 200 rpm) under a range of test loads (10, 20, 30, and 40 N). Microstructural characterization and phase analysis of the as-cast Mg-Sn alloys using scanning electron microscope and x-ray diffraction, respectively, have revealed the refinement of the binary alloy microstructure in terms of smaller dendritic arm spacing, uniform and discrete distribution of eutectic phase mixture at the interdendritic locations owing to the alloying additions. Moreover, a significant improvement in microhardness is achieved with increase in amount (wt.%) of alloying elements, depicting the highest hardness in the Mg-10Sn-3Al-1Zn (wt.%) alloy. Simultaneously, the alloying addition even in micro-concentration has been found to reduce the specific wear rate than that of the binary alloy over the entire loading range. The post-wear topographical surface features and chemical analysis using scanning electron microscope and energy-dispersive x-ray spectroscopy of the investigated alloys have suggested the oxidation and abrasion as dominant wear mechanisms. The reduced wear rates in the Al containing alloys are ascribed to the protective and continuous mechanically mixed oxide scale formation during test, which acts as a lubricating layer between the pin and the rotating disk. The discrete oxide island formation at the Zn-lean regions of Zn containing alloys is responsible for their accelerated wear rates.

Effects of Loading and Sliding Speed on the Dry Sliding Wear Behavior of Mg-3Al-0.4Si Magnesium Alloy

Wear Behaviour and Microstructural Changes of SiCw-Al Composite under Unlubricated Sliding Friction

Dry sliding wear behavior of cast Mg–11Y–5Gd–2Zn magnesium alloy

Dry sliding wear of MA/PM Al-10Ti alloy

Effect of load and sliding velocity on wear behaviour of magnesium AZ91D composites reinforced with Ca 2 SiO 4 at ambient temperature

Effects of silicon content and test conditions on the dry wear behaviour of Zn–30Al–3Cu–(0–5)Si Alloys

Effect of Alloying Elements on the Dry Sliding Wear Characteristics of Gravity-Cast Mg-Sn Based Alloys

Microstructure and Sliding Wear Behavior of PM Alloy Al10Ti after Thermal Exposure

Dry sliding wear of PM Al-10Ti alloy

Effects of cold deformation on the low speed sliding wear of the RS/PM Al–10 wt.% Ti alloy against carbon steel

Investigating the load and temperature-dependent dry sliding wear performance of Al–12Ce alloys with Si and Mg additions

Effect of Cold Deformation on Low Speed Sliding Wear of Al-10Ti Alloy

Unidirectional dry sliding wear analysis of ZE41 magnesium alloy

Contributions of the Particulate Reinforcement to Dry Sliding Wear Resistance of Rapidly Solidified Al-Ti Alloys

Effect of Different Mg2Si Concentrations on the Wear Properties and Microstructure of Mg2Si/Al–5 wt.% Cu Composites

An Experimental Investigation into the Dry Reciprocating Wear Behavior of Additively Manufactured AlSi10Mg Alloys

Effect of Heat Treatment on the Dry Sliding Wear Behavior of the Mg-3Zn-0.4Ca Alloy for Biodegradable Implants

Effect of Si Content on the Dry Sliding Wear Properties of Spray-Deposited Al–Si Alloy

Dry sliding wear behavior of additively manufactured CoCrWNixAly alloys

Relation of normal load with test temperature at mild–severe wear transition state for Mg–Gd–Y–Zr alloy

Solutionizing Temperature Effect on the Dry Sliding Wear Performance of Al-7Si-0.3Mg-3Ni Hypoeutectic Alloy