In-Situ Electrochemical Corrosion Behavior of Nickel-Base 718 Alloy under Various CO2 Partial Pressures at 150 and 205 °C in NaCl Solution

Yubi Zhang,Yongtao Zhao,An Tang,Wenjie Yang,Enzuo Li

DOI: https://doi.org/10.1007/s12540-018-0087-6

IF: 3.451

2018-01-01

Metals and Materials International

Abstract:The electrochemical corrosion behavior of nickel-base alloy 718 was investigated using electrochemical impedance spectroscopy and potentiodynamic polarization techniques at various partial pressures of CO2 (\(P_{{{\text{CO}}_{2} }}\)s) in a 25 wt% NaCl solution at 150 and 205 °C. The passive films composed of FeCO3 exhibit good corrosion resistance with a feature of Warburg impedance, Tafel plots show a complete passivation and the anodic reactions was dominated by a diffusion process at low \(P_{{{\text{CO}}_{2} }}\)s (1.8–9.8 MPa) at 150 °C. While numerous dented corrosion areas appeared on the sample surface for the \(P_{{{\text{CO}}_{2} }}\) of 11.6 MPa at 205 °C, the Tafel plot with three anodic peaks and the Nyquist diagram with an atrophied impedance arc were present. This dented corrosion attribute to the synergistic effects of stress, temperature, \(P_{{{\text{CO}}_{2} }}\) and Cl−, the temperature and stress could play crucial roles on the corrosion of the alloy 718.