Abstract:This study investigates corrosion of Fe–Ni-based alloy 800H that were exposed to supercritical CO2 (sCO2), ambient air and argon gas at pressures up to 20 MPa, at 650 and 750 °C for up to 1000 h. This alloy and other comparable metal alloys are expected to be used in sCO2 heat exchanger cycles as proposed in the DOE Advanced Ultra-Supercritical program. Alloy 800H is considered for this application, because it meets the high-temperature strength and creep rupture requirements and is a lower cost alternative to other Ni-based alloys. The oxidation performance and microstructural changes due to exposure in sCO2 have been evaluated and compared with exposures in air and Ar. The 800H alloy showed similar oxide scale thicknesses in sCO2 as in air. A recrystallized zone was observed beneath the oxide formed in air and sCO2. No such zone was observed after exposure to Ar, suggesting this recrystallization was associated with the oxidation process and not simply an effect of surface finishing. A wider recrystallized zone was observed underneath the oxide formed in sCO2 than in air. The effect of air and sCO2 on internal oxidation and carburization was investigated as well, showing that air led to more internal oxidation but less internal carburization than sCO2. It was concluded that the carbon species provided by the sCO2 atmosphere in conjunction with the increased grain boundary density in the recrystallized zone allowed for more ingress of carbon into the base metal, which resulted in a higher densities of carbides beneath the oxide scale.

Review on the Corrosion Behaviour of Nickel-Based Alloys in Supercritical Carbon Dioxide under High Temperature and Pressure

Review on corrosion of alloys for application in supercritical carbon dioxide brayton cycle

Study on Corrosion Characteristics of Heat-resistant Materials in Supercritical Carbon Dioxide Environment Containing Oxygen Impurities

State of the art overview material degradation in high-temperature supercritical CO 2 environments

Revealing the Effect of O2, SO2 and H2O in Supercritical CO2 on the Corrosion Behavior of 316L Steel at Elevated Temperature

Review of corrosion behavior of metal materials in supercritical carbon dioxide environment

Corrosion Behaviors of Heat-Resisting Alloys in High Temperature Carbon Dioxide

Corrosion Characteristics and Mechanisms of Typical Ni-based Corrosion-Resistant Alloys in Sub- and Supercritical Water

Overview on corrosion in supercritical fluids

Corrosion Performance of Heat-Resisting Steels and Alloys in Supercritical Carbon Dioxide at 650 °C and 15 MPa

Corrosion behaviors of steels under supercritical CO2 conditions

Effects of Corrosion in Supercritical CO2 on the Microstructural Evolution in 800H Alloy

Corrosion and Mechanical Performance of Grade 92 Ferritic-Martensitic Steel After Exposure to Supercritical Carbon Dioxide

Corrosion Properties of Candidate Materials in Supercritical Water Oxidation Process

Corrosion and creep behavior of a Ni-base alloy in supercritical-carbon dioxide environment at 650 °C

Compatibility of Different Commercial Alloys in High-Temperature, Supercritical Carbon Dioxide

High-Temperature Corrosion Behaviors of Ni-Based Alloys in Carbon Dioxide

A review on corrosion inhibitors for high-pressure supercritical CO2 environment: Challenges and opportunities

Thermodynamic Analysis of Typical Alloy Oxidation and Carburization in High-Temperature CO2 Atmosphere

Evaluation of Supercritical Carbon Dioxide Corrosion by High Temperature Oxidation Experiments and Machine Learning Models

Corrosion of Alloy Haynes 230 in High Temperature Supercritical Carbon Dioxide with Oxygen Impurity Additions