Abstract:Ni3Al‐based superalloys are thermally exposed to a CO2 atmosphere at 600°C/5 MPa, and the changes that occur in the alloy during the initial period of thermal exposure are investigated. The corrosion and carburization behaviors and mechanisms were investigated in detail. The results show that harmful elements do not further enter the matrix, indicating that Ni3Al‐based superalloys show good corrosion and carburization resistance during thermal exposure. (a) transmission electron micrograph of the sample after 500 h thermal exposure; (b) energy dispersive spectroscopy (EDS) mapping results in (a); (c) EDS line scan result; (d) delamination phenomenon of the oxide layer and EDS mapping results; (e) selected area electron diffraction (SAED) pattern of region | in (d); (f) SAED pattern of region || in (d). To investigate the application of Ni3Al‐based superalloys in gas turbine cycle systems, this experiment exposed Ni3Al‐based superalloys to a 600°C/5 MPa environment with 99.995% pure CO2 gas. The corrosion and carburization behaviors and mechanisms were investigated in detail. The results reveal that with prolonged thermal exposure, the surface oxides of the samples tend to develop a continuous and homogeneous transition state alumina layer. This layer serves as a protective barrier, preventing the penetration and corrosion of external carbon‐containing and oxygen‐containing substances into the matrix. A small amount of carbon‐containing hazardous substances still penetrates the oxide layer or grain boundaries through highly diffusive pathways such as nanochannels, pores, and cracks, because the transition state of alumina is not completely dense. This leads to carbon deposition at the interface between the oxide layer and the matrix, where a mixture of alumina and amorphous carbon is formed at the interface.

Alloys SS316 and Hastelloy-C276 in Supercritical CO2 at High Temperature

Revealing the Effect of O2, SO2 and H2O in Supercritical CO2 on the Corrosion Behavior of 316L Steel at Elevated Temperature

Compatibility of Different Commercial Alloys in High-Temperature, Supercritical Carbon Dioxide

Mechanical and Corrosion Response of 316SS in Supercritical CO2

Corrosion of Alloy Haynes 230 in High Temperature Supercritical Carbon Dioxide with Oxygen Impurity Additions

Study on Corrosion Characteristics of Heat-resistant Materials in Supercritical Carbon Dioxide Environment Containing Oxygen Impurities

Corrosion Performance of Heat-Resisting Steels and Alloys in Supercritical Carbon Dioxide at 650 °C and 15 MPa

Effects of Corrosion in Supercritical CO2 on the Microstructural Evolution in 800H Alloy

Corrosion and Mechanical Performance of Grade 92 Ferritic-Martensitic Steel After Exposure to Supercritical Carbon Dioxide

Corrosion and carburization of Ni3Al‐based superalloys in high‐temperature carbon dioxide

Corrosion and Carburization Behavior of Heat-Resistant Steels in a High-Temperature Supercritical Carbon Dioxide Environment

Evaluation of coated steels in supercritical CO2

Effect of Supercritical CO2 on Steel Ductility at 450°-650°C

Corrosion Performance of Austenitic Super 304H in Supercritical CO 2 at Different Temperatures and O 2 Impurity

Comparison of the corrosion of materials in supercritical carbon dioxide, air, and argon environments

Corrosion Behaviour of Ni-based Alloys 230, 617, and 601 in CO2 Gas at 750 and 850°C

Corrosion Behavior of FBR Structural Materials in High Temperature Supercritical CO2

Corrosion Behavior of Superalloys in High Temperature Gas Cooled Reactor in Impure Helium with Corrosion Time

Effect of Cyclic Reaction on Corrosion Behavior of Chromium-Containing Alloys in CO2 Gas at 650 °C

Thermodynamic Analysis of Typical Alloy Oxidation and Carburization in High-Temperature CO2 Atmosphere

Corrosion Behavior of Heat-Resistant Materials in High-Temperature Carbon Dioxide Environment