Abstract:The supercritical carbon dioxide (s-CO2) Brayton cycle is currently being explored as a replacement for the steam Rankine cycle due to its potential for higher efficiency and lower cycle cost. 316 stainless steel is a candidate alloy for use in s-CO2 up to roughly 600 °C, but the mechanical effects of prolonged exposure of base and welded material in s-CO2 have not been analyzed. The potential for carburization makes this an important concern for the implementation of 316 and similar austenitic stainless steels in the s-CO2 environment. In this study, welded and base material of two types of 316–316L and 316H–were exposed in either s-CO2 or argon at 550 °C or 750 °C for 1000 h. 550 °C s-CO2 exposure yielded a thin (< 1 µm) Cr oxide with occasional nodules of duplex Fe oxide and Fe–Cr spinel that were up to 5 microns thick. However, tensile results from s-CO−2 exposure matched those of 550 °C thermal aging in Ar, indicating that no mechanically detrimental carburization occurred in either 316 variant after 1000 h exposure. Conversely, 750 °C s-CO2 exposure produced roughly 10 × the oxide thickness, with a more substantial Fe oxide (3–5 µm) on the majority of the surface and nodules of up to 40 µm thick. In comparison to aged samples, tensile testing of 750 °C CO2-exposed samples revealed ductility loss attributed to carburization. Projections of 316L performance in s-CO2 indicate that mechanically detrimental carburization—equal to that shown here for 750 °C, 1000 h—will likely be present after 7–14 years of service at 550 °C.

Effect of Supercritical CO2 on Steel Ductility at 450°-650°C

Revealing the Effect of O2, SO2 and H2O in Supercritical CO2 on the Corrosion Behavior of 316L Steel at Elevated Temperature

Evaluation of coated steels in supercritical CO2

Effect of Impurities On the Compatibility of Steels in Supercritical CO2 at 450°-650°c

Corrosion and Mechanical Performance of Grade 92 Ferritic-Martensitic Steel After Exposure to Supercritical Carbon Dioxide

Study on Mechanical Degradation of Ferrite/ Martensite and Austenitic Steels in High-Temperature Supercritical Carbon Dioxide Environment

Study on Corrosion Characteristics of Heat-resistant Materials in Supercritical Carbon Dioxide Environment Containing Oxygen Impurities

Mechanical and Corrosion Response of 316SS in Supercritical CO2

Corrosion Performance of Heat-Resisting Steels and Alloys in Supercritical Carbon Dioxide at 650 °C and 15 MPa

Effects of Corrosion in Supercritical CO2 on the Microstructural Evolution in 800H Alloy

Compatibility of Different Commercial Alloys in High-Temperature, Supercritical Carbon Dioxide

Temperature dependence of carbon deposits within oxide scale on CrMoV steel in atmospheric and supercritical CO2

Corrosion and Carburization Behavior of Heat-Resistant Steels in a High-Temperature Supercritical Carbon Dioxide Environment

Effect of Solution Annealing and Al Addition on the Corrosion Behavior of Austenitic Stainless Steel in Supercritical Carbon Dioxide at High Temperature

Carbon depositions within the oxide scale and its effect on the oxidation behavior of low alloy steel in low (0.1 MPa), sub-(5 MPa) and supercritical (10 MPa) CO2 at 550°C

Alloys SS316 and Hastelloy-C276 in Supercritical CO2 at High Temperature

Corrosion Behavior of Alumina-Forming Austenitic Steel in Supercritical Carbon Dioxide Conditions: Effects of Nb Content and Temperature

Corrosion Behavior of FBR Structural Materials in High Temperature Supercritical CO2

Comparison of the corrosion of materials in supercritical carbon dioxide, air, and argon environments

Corrosion Performance of Austenitic Super 304H in Supercritical CO 2 at Different Temperatures and O 2 Impurity

10000 Hours Thermal Aging Behavior and Supercritical CO2 Corrosion Performance of Candidate Cladding AFA Alloys for Novel Gas - Cooled Reactors