Abstract:Supercritical carbon dioxide is one of the most promising candidate working fluids for nuclear power plants.Structural materials using in this kind of system face severe challenges due to its high temperature and high pressure.Corrosion,especially oxidation and carburization,will occur,which leads to the failure of material.Tradi-tional metallic materials like austenitic stainless steel,which is regarded as the candidate cladding materials,will break away because of their limited properties.To further improve the corrosion resistance of austenitic stainless steel as the candidate cladding material for supercritical carbon dioxide nuclear reactor,the general corrosion behavior of three kinds of alumina-forming austenitic stainless steel with different Al contents and their Al-free steel was investigated in supercritical carbon dioxide at 650 ℃/20 MPa.The purity of carbon dioxide was 99.99％.All samples were firstly ground,and then polished to eliminate the surface damage regions.Scanning electron microscopy equipped with backscattered electron,electron backscatter diffraction detector and energy disper-sive spectroscopy was used for microanalysis.Focused ion beam system was used to prepare the cross-sectional transmission electron microscopy foils.Selected area electron diffraction was also carried out on the transmission electron microscopy foils for revealing the detailed microstructural characterization.Glow discharge optical emission spectrum was used for carburization analysis.The results show that the weight gain of materials decreases with the increase of Al content,and the weight gain of 3.5wt％Al steel is only about 0.022 mg/cm2.The weight gain against exposure time of different materials follows the parabolic growth law approximately,which indicates that the corrosion behavior is mainly controlled by diffusion.When the content of Al is less than 1.5wt％,a dual-layer Fe-rich oxide film is formed on the surface with poor protection.Some pores were observed within it,which can cause oxidation and carburization.Carburization occurs on Al-free steel and the depth of the carburization region can be up to about 12 µm.When the content of Al is higher than 2.5wt％,protective oxide films are formed on the surface.Its outer layer is mainly rich in Cr and the inner layer is rich in Al.The Al layer on 2.5wt％and 3.5wt％Al containing steel is more continuous.These oxides own better corrosion resistance than that formed on 1.5wt％steel.Although more protective oxides are formed,carburization still exists in the oxide film and matrix of this kind of materials,while the thickness of the carburization region decreases to about 6 μm.Higher Al content,above 2.5wt％,can effectively facilitate the formation of protective Al-rich oxide film,which hinders the outward diffusion of Fe and the inward diffusion of C.It further improves the oxidation and carburizing resist-ance of materials,which will be useful in the supercritical carbon dioxide nuclear power plant.

Corrosion Behavior of Alumina-Forming Austenitic Steel in Supercritical Carbon Dioxide Conditions: Effects of Nb Content and Temperature

Revealing the Effect of O2, SO2 and H2O in Supercritical CO2 on the Corrosion Behavior of 316L Steel at Elevated Temperature

Corrosion behavior and failure mechanism of amorphous Al2O3 coating at high-temperature LBE

On the role of Al/Nb in the SCC of AFA stainless steels in supercritical CO 2

Microstructures, Tensile Properties and Corrosion Behaviors of Fe20Cr25NiNb Stainless Steels with Different Al Contents in Supercritical Carbon Dioxide

Effects of Nb on Creep Properties and Hot Corrosion Resistance of New Alumina-Forming Austenitic Steels at 700 °C

Effect of Solution Annealing and Al Addition on the Corrosion Behavior of Austenitic Stainless Steel in Supercritical Carbon Dioxide at High Temperature

Effect of Al Content on General Corrosion Behavior of Alumina-forming Austenitic Stainless Steel in High Temperature Supercritical Carbon Dioxide

Corrosion Behavior of Nb-doped FeCrAl Alloy in 500°C Steam

Corrosion behavior of a new alumina-forming duplex stainless steel with different surface treatment in supercritical carbon dioxide

New insights into the initial oxidation behavior of an ultra-corrosion resistant alumina-forming austenitic steel in supercritical carbon dioxide: the effects of precipitated intragranular intermetallic compounds

Oxide Scale Growth Behavior of Alumina-Forming Austenitic Stainless Steel Exposed to Supercritical Water

Corrosion Behaviour of Ni-based Alloys 230, 617, and 601 in CO2 Gas at 750 and 850°C

CORROSION BEHAVIOR OF SUPER-AUSTENITIC STAINLESS STEEL AL-6XN IN SUPERCRITICAL WATER

Corrosion Behavior of a Novel Alumina Forming Austenitic Steel Exposed to Supercritical Water

Effect of Mn content on the high-temperature oxidation behaviors of Mn-substituted-for-Ni alumina-forming austenitic stainless steel

Anomalous Oxidation Rate-Temperature Dependence of Alumina-Forming Austenitic Stainless Steels Exposed to 500 - 600 °C Supercritical Water

Irradiation accelerated corrosion of alumina-forming austenitic steels in supercritical CO2: The oxide scale formed within an individual grain or affected by grain boundary

Irradiation accelerated corrosion of alumina-forming austenitic steels in supercritical CO 2 : the oxide scale formed within an individual grain or affected by grain boundary

Study on the Corrosion Behavior of Aluminum Reinforced Austenitic Steel in Liquid Lead Bismuth at 550 °C

Effect of Nb Addition on Oxidation Mechanisms of High Cr Ferritic Steel in Ar–H2–H2O