Effect of Heat Treatment on Microstructure, Mechanical, and Corrosion Properties of Squeeze Cast Al 319.0 Alloy
Yogendra Mahton,Vibhav Jha,Partha Saha
DOI: https://doi.org/10.1007/s40962-023-01030-9
2023-04-29
International Journal of Metalcasting
Abstract:The aim of this work is to investigate the effect of heat treatment (T6) on the microstructure, mechanical, and corrosion properties of Al 319.0 alloy. In particular, Al 319.0 alloy is developed by squeeze casting using 200 MPa pressure, and further the ingots are solutionized, quenched and artificially aged to develop a homogenous microstructure, improve distribution of secondary phase(s), and mechanical properties at ambient and elevated temperatures. The phase and microstructure of the as-cast and heat-treated Al 319.0 alloys analyzed using X-ray diffraction, optical microscope, and field emission scanning electron microscope illustrate cast ingot contain α -Al as a primary phase and Al 2 Cu, eutectic Si, and Al 5 Si 7 Cu-containing intermetallic as secondary phase(s). However, heat treatment leads to complete dissolution of Al 5 Si 7 Cu and partial dissolution and re-precipitation of Al 2 Cu phase. Moreover, heat treatment changes the morphology of eutectic Si into spheroidal Si, blocky Al 2 Cu into spheroids Al 2 Cu, and the heat-resistant α (FeMn), Al 8 Cu 3 Mn(Si) phases emerged. The tensile test at room and elevated temperatures exhibit significant improvement in the YS and UTS at ambient temperature in heat-treated alloy owing to the presence of precipitation-hardened phases. Importantly, these phases are found stable up to 150 °C and tend to coarsen at 250 °C owing to thermal softening invariably leading to a substantial reduction in mechanical properties. Potentiodynamic polarization and electrochemical impedance spectroscopy shed light on galvanic corrosion phenomena predominant in 0.1 M NaCl solution. In particular, heat-treated alloy specimens demonstrated the lowest corrosion current ( I corr —~1.72 μA/cm 2 ) , and highest polarization resistance ( R p —12260 Ω.cm 2 ) implying superior corrosion resistance as compared to as-cast alloy owing to protective barrier provided by finer Al 2 Cu precipitates and spheroidal Si.
metallurgy & metallurgical engineering