Abstract:Ni3Al‐based superalloys are thermally exposed to a CO2 atmosphere at 600°C/5 MPa, and the changes that occur in the alloy during the initial period of thermal exposure are investigated. The corrosion and carburization behaviors and mechanisms were investigated in detail. The results show that harmful elements do not further enter the matrix, indicating that Ni3Al‐based superalloys show good corrosion and carburization resistance during thermal exposure. (a) transmission electron micrograph of the sample after 500 h thermal exposure; (b) energy dispersive spectroscopy (EDS) mapping results in (a); (c) EDS line scan result; (d) delamination phenomenon of the oxide layer and EDS mapping results; (e) selected area electron diffraction (SAED) pattern of region | in (d); (f) SAED pattern of region || in (d). To investigate the application of Ni3Al‐based superalloys in gas turbine cycle systems, this experiment exposed Ni3Al‐based superalloys to a 600°C/5 MPa environment with 99.995% pure CO2 gas. The corrosion and carburization behaviors and mechanisms were investigated in detail. The results reveal that with prolonged thermal exposure, the surface oxides of the samples tend to develop a continuous and homogeneous transition state alumina layer. This layer serves as a protective barrier, preventing the penetration and corrosion of external carbon‐containing and oxygen‐containing substances into the matrix. A small amount of carbon‐containing hazardous substances still penetrates the oxide layer or grain boundaries through highly diffusive pathways such as nanochannels, pores, and cracks, because the transition state of alumina is not completely dense. This leads to carbon deposition at the interface between the oxide layer and the matrix, where a mixture of alumina and amorphous carbon is formed at the interface.

High-temperature corrosion resistance of nickel-base alloy 617 in supercritical carbon dioxide environment

The oxidation behavior of nickel‐based alloy Inconel 617 in supercritical water

Study on Corrosion Characteristics of Heat-resistant Materials in Supercritical Carbon Dioxide Environment Containing Oxygen Impurities

Revealing the Effect of O2, SO2 and H2O in Supercritical CO2 on the Corrosion Behavior of 316L Steel at Elevated Temperature

Chlorine-Induced High Temperature Corrosion of Inconel 625 Alloy with the Addition of Yttrium at 800 °C

Compatibility of Different Commercial Alloys in High-Temperature, Supercritical Carbon Dioxide

CORROSION STUDY OF INCONEL 617 ALLOY IN HTGR WITH IMPURE HELIUM ATMOSPHERE

Corrosion Behaviour of Ni-based Alloys 230, 617, and 601 in CO2 Gas at 750 and 850°C

Oxidation Behavior and Tensile Property of Inconel 617 in the Simulation Environment of the Very-High-Temperature Reactor

Effects of Corrosion in Supercritical CO2 on the Microstructural Evolution in 800H Alloy

Corrosion and carburization of Ni3Al‐based superalloys in high‐temperature carbon dioxide

Corrosion and creep behavior of a Ni-base alloy in supercritical-carbon dioxide environment at 650 °C

Microstructural understanding of high-temperature oxidation behaviour of selective laser melted Inconel 718 superalloy in CO 2 atmosphere

Investigation of the fatigue damage mechanism of Inconel 617 at elevated temperatures obtained by in situ SEM fatigue tests

Investigation on Wear Resistance and Corrosion Resistance of Electron Beam Cladding Co-Alloy Coating on Inconel617

Effect of temperature and medium environment on corrosion fatigue behavior of Inconel 625

Mechanical and Corrosion Response of 316SS in Supercritical CO2

Corrosion Studies of Inconel 617 in High Temperature Air and He-ppmO2 Atmospheres

Oxidation resistance of nickel-based superalloy Inconel 600 in air at different temperatures

Corrosion and Carburization Behavior of Heat-Resistant Steels in a High-Temperature Supercritical Carbon Dioxide Environment

Degradation of nickel-based alloys for precise casting in high-temperature gas environment