Abstract:As MOSFET devices are scaled down to below 100nm, the gate oxide thickness is required below 2nm. Conventional SiO2 gate dielectric will be replaced due to excessive leakage and poor reliabilit y. Thus, high dielectrics constant (K) gate dielectrics are being studied as an alternative. High-K dielectrics materials such as CeO2, Y2O3, Ta2O5, HfO2, ZrO2, TiO2, Al2O3, SrTiO3(STO), and BaSrTiO3(BST) have are studied . Among them, HfO2 is a promising candidate due to its thermodynamic stabil ity on Si, high dielectric constant ( 25), and relatively large band gap (5.68eV). In the paper, ultra-thin HfO2 gate dielectrics films were fabricated, electrical and reliabili ty properties such as capacitance-voltage (C-V), current-voltage (I-V), stress induce leakage current (SILC) effects and breakdown characteristics were studied. In the experiment, HfO2 capacitor samples have been fabricated using the following process. P-type (100) sili con substrates with 5-8 cm resistivity were cleaned using H2SO4:H2O2 (2:1) solution and HF dip. Thin HfO2 layers were following deposited at room temperature by ion beam sputtering a sintered HfO2 target. Then they were annealed under various temperatures and ambient. After annealing, Pt top electrodes were deposited by sputtering. The area of the capacitors was 5 10cm. The C-V and I-V curves were measured using HP4156B semiconductor parameter analyzer and Keithley590 C-V analyzer. Figure 1 shows the capacitance-voltage (C-V) curves of HfO2 gate dielectrics. The largest value of measured capacitance density in accumulation is Cmax/A=11.6fF/ m. The equivalent oxide thickness (EOT) is about 2.9nm. Comparing capacitances of various annealing temperatures, the capacitance of the sample annealed at 400 is highest. With increase annealed temperatures, EOT increased. Figure 2 shows the current-voltage (I-V) characteristics of HfO2 gate dielectrics. The leakage current of the sample annealed at 800 is lowest, which is about 3.09 10A/cm at –1.5V gate voltage. No distinct SILC effect is obtained. The leakage current of the sample annealed at 400 after 1×10C/cm stress has a very lit tle diversification. With increase annealed temperatures, the leakage current and SILC effect reduced. Figure 3 shows breakdown characteristics of HfO2 dielectrics. The breakdown electric field of HfO2 dielectrics is more than 2×10MV/cm. With increase annealing temperatures, the breakdown voltages decreased. Consequently, ultra-thin HfO2 gate dielectrics (EOT<3nm) were fabricated. All samples annealed under various temperatures and N2 ambient have good electrical characteristic and reliabili ty. With increase annealing temperatures, EOT of increased, the leakage current and SILC effect reduced, the breakdown voltages decreased. References: [1] E.P. Gusev, E. Carier, D.A. Buchanan, M. Gribelyuk, M. Copel, H. Okorn-Schmidt, and C.D. Emic, Microelectronic Engineering 59(2001) 341-349 [2] Wen-jie Qi, Renee Nieh, Byoung Hun Lee, Laegu Kang, Yongjoo Jeon, and Jack C. Lee, Applied Physics Letters, 2000, 77(20): 3269-3271 [3] G.D. Wilk, and R.M. Wallace, Applied Physics Letters, 1999, 74(19): 2854-2856 [4] Kevin X. Zhang, Carlton M. Osbun, IEEE Trans. Electron Devices, 42(12), 1995, 2181-2188 [5] G.D. Wilk, R.M. Wallace, J.M. Anthony, Applied Physics Review, 2001, 89(10): 5243-5275

Low-temperature solution-based fabrication of high-k HfO 2 dielectric thin films via combustion process

Microstructure, Optical, Electrical Properties, and Leakage Current Transport Mechanism of Sol–gel-Processed High-K HfO2 Gate Dielectrics

Annealing Temperature Dependence on the Structural and Optical Properties of Sputtering-Grown High-K HfO2 Gate Dielectrics

Microstructure, Optical and Electrical Properties of Sputtered HfTiO High-K Gate Dielectric Thin Films

Microstructure, optical and electrical properties of solution-derived peroxo-zirconium oxide gate dielectrics for CMOS application

Oxygen incorporated solution-processed high-kappa La2O3 dielectrics with large-area uniformity, low leakage and high breakdown field comparable with ALD deposited films

Solution Processable High Quality ZrO2 Dielectric Films for Low Operation Voltage and Flexible Organic Thin Film Transistor Applications

Solution-Driven HfLaO x -Based Gate Dielectrics for Thin Film Transistors and Unipolar Inverters

Electrical and Reliability Characteristics of High-Κ HfO 2 Gate Dielectrics

High Mobility Thin-Film Transistor with Solution-Processed Hafnium-Oxide Dielectric and Zinc-Indium-Tin-Oxide Semiconductor

Room‐Temperature Fabrication of High‐Quality Lanthanum Oxide High‐κ Dielectric Films by a Solution Process for Low‐Power Soft Electronics

Thin Hfo2 Films Grown on Si(100) by Atomic Oxygen Assisted Molecular Beam Epitaxy

Fabrication and Characterization of Pulsed Laser Deposited Hfo2 Films for High-K Gate Dielectric Applications

Thermal Stability and Electrical Properties of Pulsed Laser Deposited Hf–aluminate Thin Films for High-K Gate Dielectric Applications

Novel halogenated cyclopentadienyl hafnium precursor for atomic layer deposition of high-performance HfO2 thin film

Thermal and Voltage Instabilities of Hafnium Oxide Films Prepared by Sputtering Technique

All-Water-Driven High-k HfO2 Gate Dielectrics and Applications in Thin Film Transistors

Phase Separation and Interfacial Reaction of High-K HfAlOx Films Prepared by Pulsed-Laser Deposition in Oxygen-Deficient Ambient

Solution Processable Amorphous Hafnium Silicate Dielectrics and Their Application in Oxide Thin Film Transistors

Comparative Study of Pulsed Laser Deposited HfO 2 and Hf–aluminate Films for High- K Gate Dielectric Applications

Surface Modification on Solution Processable ZrO2 High-k Dielectrics for Low Voltage Operations of Organic Thin Film Transistors