Abstract:At present, 5 G communication is developing rapidly, devices are becoming miniaturized, which requires the continuous emergence of materials with high dielectric constant. In this work, choosing Co2+ to sub-stitute Li1-2xCoxNb0.6Ti0.5O3 (LCNT, 0 <= x <= 0.1) + 0.4 wt% LBSCA ceramics successfully achieved high per-mittivity er and temperature stable resonant temperature frequency coefficient Tau f sintered at 950 degrees C, including er similar to 62, Qxf similar to 6255 GHz, and Tau f similar to 0.97 ppm/degrees C (x = 0.02), er similar to 56.55, Qxf similar to 7090 GHz, and Tau f similar to- 28.07 ppm/degrees C (x = 0.06). Meanwhile, the influence of Co2+ on LNT ceramics for phase composition, micro-structure, microwave dielectric performance and Raman vibration had been studied in detail. All samples belonged to M phase. Rod-like or blocky grains were gradually refined, indicating that Co2+ had the effect of grain refinement. In microwave dielectric performance, ionic polarizability played a leading role in er, Qxf value was positively correlated with the bulk density, Tau f directly depended on the average repeatable layer N. In Raman spectroscopy, three modes of Raman vibration had been identified as translation or rotation of Li+ ions, Nb/Ti bond vibration, [Nb/TiO6] octahedral vibration. To meet low temperature co-fired applications, the LCNT (x = 0.02) ceramic didn't react with Ag, which suggested it was achieving candidates for the next generation of medium K LTCC materials.(c) 2022 Elsevier B.V. All rights reserved.

A new niobate-based CaO–2CuO–NbO microwave dielectric ceramic composite for LTCC applications

A new niobate-based CaO–2CuO–Nb 2 O 5 microwave dielectric ceramic composite for LTCC applications

A New Microwave Dielectric Ceramic for LTCC Applications

Ultralow-loss (1-x)CaWO4-xNa2WO4 (x = 0.1, 0.2) microwave dielectric ceramic for LTCC applications

A new high-Q×f Li4NbO4F microwave dielectric ceramic for LTCC applications

Simultaneously achieving high permittivity and low loss in CuO/Nb2O5 substituted Li2O-TiO2-Nb2O5 low-temperature microwave dielectric ceramics

Developing high performance, low temperature sintering and temperature stable K40 material in Co2O3/Nb2O5-modified Ba3Ti4Nb4O21 microwave dielectric ceramics for 5G-LTCC communication devices

A low-sintering temperature microwave dielectric ceramic for 5G LTCC applications with ultralow loss

Microwave dielectric characterization and densification mechanism analysis of CaO‐B2O3‐SiO2 glass‐ceramic/Al2O3 composites for LTCC applications

Temperature stable Li5.5Nb1.5O6F-based microwave dielectric ceramics for LTCC applications

A Novel LiNb0.6Ti0.5O3 Microwave Dielectric Ceramic with Ca Substitutions

Sintering and microwave dielectric properties of Ba1−xCaxNi2V2O8 ceramics for LTCC applications

Medium K and Temperature-Stable Co2+-substituted LiNb0.6Ti0.5O3 Microwave Dielectric Ceramics for LTCC Miniaturized Applications

A New Microwave Ceramic with Low-Permittivity for Ltcc Applications

Microwave Dielectric Properties of the Low-Temperature-fired Li2ZnTi3O8–Li2TiO3 Ceramics for LTCC Applications

Low Temperature Sinter-Ability of Microwave Dielectric Ceramics 0.4(Ca<sub>0.61</sub>Nd<sub>0.26</sub>)TiO<sub>3</sub>-0.6(Li<sub>0.5</sub>Sm<sub>0.5</sub>)TiO<sub>3</sub>

Calcium Manganese Vanadate Microwave Dielectric Ceramics with Ni2+ Partial Substitution for LTCC Applications

LiCa3ZnV3O12: A Novel Low-Firing, High Q Microwave Dielectric Ceramic

Microwave dielectric properties of the 5.7Li 2 O–Nb 2 O 5 –7.3TiO 2 ceramics

Novel series of high-Q oxyfluoride microwave dielectric ceramics for LTCC applications

A novel low firing microwave dielectric ceramic NaCa2Mg 2V3O12