Calcium Manganese Vanadate Microwave Dielectric Ceramics with Ni2+ Partial Substitution for LTCC Applications

Minshu Chen,Yuanxun Li,Fuyu Li

DOI: https://doi.org/10.1007/s11664-024-10943-y

IF: 2.1

2024-02-16

Journal of Electronic Materials

Abstract:Here, Ca5Mn4−xNixV6O24 (CMNVO, x = 0.00–0.08) ceramics are successfully prepared by the solid-phase reaction method, and the connection between the physical phase information, microscopic morphology, Raman spectroscopy, and microwave dielectric properties is explored. The experimental results show that Ni2+ occupies the Mn2+ sites without altering the crystal structure and is effectively solid-solvated into the lattice. The relative density reaches a maximum value of 95.9% when the temperature (Tem.) = 900°C and x = 0.06. The trend of the dielectric constant (εr) depends on the ionic polarization rate, and the quality factor (Q×f values) are correlated with the microstructure and relative density. The maximum value of 43,800 GHz is reached at Tem. = 900°C and x = 0.06, and the temperature coefficient of resonant frequency (τf values) is enhanced from −75 ppm/°C to −52 ppm/°C. The CMNVO (x = 0.06) ceramic obtains better microwave dielectric properties (εr = 11.4, Q×f = 43,800 GHz, and τf = −52 ppm/°C). This ceramic material is expected to be a candidate for low-temperature co-fired ceramic (LTCC) microwave devices.

engineering, electrical & electronic,materials science, multidisciplinary,physics, applied