Enhancement of dielectric properties in MnTiNb2O8-Based microwave ceramic materials

Ming Huang,Jinxian Zhang,Yu Tang,Haijun Mao,Zhuofeng Liu,Wei Li,Fenglin Wang,Weijun Zhang,Xingyu Chen

DOI: https://doi.org/10.1016/j.ceramint.2024.01.103

IF: 5.532

2024-04-01

Ceramics International

Abstract:A novel MnTiNb2O8-based microwave dielectric ceramic was synthesized by solid-state route and its microwave dielectric properties were investigated. The effects of excess Mn2+ on the microstructure and microwave dielectric properties of Mn x TiNb2O8 (x = 1.00–1.20) were investigated. The X-ray diffraction and scanning electron microscopy results showed that MnTiNb2O8 was the dominant crystalline phase in all samples, but TiO2, as a second phase, was consistently present. The complex impedance spectroscopy and X-ray photoelectron spectroscopy analysis suggested that the addition of a small amount of Mn could inhibit the formation of oxygen vacancies and hinder the reduction of Ti4+. The study found that by adding a small amount of Mn, the quality factor (Q × f) of ceramics can be significantly improved without affecting the dielectric constant (ε r), thereby greatly optimizing the dielectric properties of ceramics. Subsequently, the temperature coefficient of resonant frequency (τ f ) of the ceramic was successfully adjusted to near zero by adding a small amount of Zr4+ instead of Ti4+. Among all Mn x Ti1-y Zr y Nb2O8 (x = 1.00–1.20, 0 ≤ y ≤ 0.28) ceramics, samples with x = 1.05 and y = 0.1 sintered at 1200 °C showed the best microwave dielectric properties: ε r = 32.9, Q × f = 11,427 GHz, and τ f  = 0 ppm/°C.

materials science, ceramics